以硫脲、乙氧基次甲基丙二酸二乙酯和甲基丙烯酸ω-羟癸酯为主要原料合成了一种新的粘接性单体10-甲基丙烯酰氧癸基-2-硫脲嘧啶-5-羧酸酯. 用1H NMR、MS和FT-IR测试技术对产物结构进行了表征,通过剪切强度的测试评价了其对复合树脂与高含金合金、钛合金和钴铬合金之间的粘接所起到的作用. 结果表明,10-甲基丙烯酰氧癸基-2-硫脲嘧啶-5-羧酸酯能够促进复合树脂与高含金合金的粘接,当其质量分数为0.5%时,剪切强度达到最大22.4 MPa,但此单体并不能促进钛合金和钴铬合金与复合树脂之间的粘接,剪切强度分别为12.1和13.7 MPa.
参考文献
| [1] | Kojima K.J J Dent Mater[J],1986,5:92 |
| [2] | Kojima K,Kadoma Y,Imai Y.J J Dent Mater[J],1987,6:702;1987,6:112 |
| [3] | Kadoma Y,Kojima K.J J Dent Mater[J],1992,11:940 |
| [4] | Kojima K,Kadoma Y.J J Dent Mater[J],1992,11:234 |
| [5] | Kadoma Y.J J Dent Mater[J],1997,16:114 |
| [6] | Kadoma Y.J J Dent Mater[J],1995,14:697 |
| [7] | SHI Yan-Hong(石艳红),LI Guo-Ming(李国明),HUANG Qiao(黄巧).Chinese J Appl Chem(应用化学)[J],2005,7:804 |
| [8] | HE Chu-Hua(贺楚华),LIU Chuan-Xiang(刘传湘),FU Shi-Fu(付仕福),et al.Appl Chem Ind(应用化工)[J],2003,4:40 |
| [9] | Ishida T,Choi N,Mizutani W,et al.Langmuir[J],1999,15:6 799 |
| [10] | Chechik V,Schonherr H,Vancso G J.Langmuir[J],1998,14:3 003 |
| [11] | Hasan M,Bethell D,Brust M.J Am Chem Soc[J],2002,124:7 |
| [12] | Chang S-C,Chao I,Tao Y-T.J Am Chem Soc[J],1994,116:6 792 |
| [13] | Atsuta M.6th Meeting of the International College of Prosthodontists[C].Califomia:San Diego,1995:19 |
| [14] | Suzuki M,Fujishima A,Miyazaki T,et al.Biomaterials[J],1999,20:839 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%