研究了原位聚合法制备的炭黑/气相生长炭纤维/聚甲基丙烯酸丁酯(CB/VGCF/PBMA)复合材料的导电性和在饱和有机蒸气中的电阻响应性能. 结果表明,通过加入质量分数为1%的VGCF即可使炭黑/聚甲基丙烯酸丁酯复合材料的电阻率1 040 Ω·cm降至195 Ω·cm,在这种三元复合体系中存在一种二阶逾渗效应;而且能使复合材料的负蒸气系数效应(NVC)强度从15.6降至2.2.
参考文献
[1] | Albert K J,Lewis N S,Schauer C L,et al.Chem Rev[J],2000,100:2 595 |
[2] | SHEN Lie(沈烈),XU Jian-Wen(徐建文),YI Xiao-Su(益小苏).Acta Mater Compositae Sin(复合材料学报)[J],2001,3(18):18 |
[3] | Jia W,Tchoudakov R,Joseph R,et al.Polym Compos[J],2002,23(4):510 |
[4] | Koscho M E,Grubbs R H,Lewis N S.Anal Chem[J],2002,74:1 307 |
[5] | Chen J,Iwata H,Tsubokawa N,et al.Polymer[J],2002,43:2 201 |
[6] | Feller J F,Grohens Y.Sensors and Actuators B[J],2004,97:231 |
[7] | Dong X M,Fu R W,Zhang M Q,et al.Polym Bull[J],2003,50:99 |
[8] | Srivastava S,Tchoudakov R,Narkis M.Polym Eng Sci[J],2000,40:1 522 |
[9] | HE Fu(贺福),Chief-Edr(编著).Carbon Fibres and its Application Technology(碳纤维及其应用技术)[M],Chapt.6 (第6章).Beijing(北京):Chemical Industry Press(化学工业出版社),2004:189 |
[10] | Zhang M Q,Yu G,Zeng H M,et al.Macromolecules[J],1998,61:6 724 |
[11] | Tang H,Chen X,Luo Y.Eur Polym J[J],1997,33(8):1 383 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%