采用羟丙基甲基纤维素(HPMC)为软模板,在CaCl2、Na2CO3体系中调控合成了球霰石型的碳酸钙球形晶体.研究了碳酸钙球体的成型原因,分析了不同浓度HPMC对晶体生长的影响;分别用SEM、XRD和FT-IR测试技术对晶体的形貌和结构进行了观察和表征.结果表明,在纯水溶液中所得的碳酸钙为菱形方解石;HPMC的加入促使球霰石相碳酸钙的异相成核,碳酸钙的晶型与形貌随HPMC质量分数的变化而改变,当HPMC的质量分数达到1.0%时,可成功地诱导碳酸钙晶体取向生长形成球体.
参考文献
| [1] | Smith B L.Nature[J],1999,399:761 |
| [2] | Shenton W,Douglas T,Young M,et al.Adv Mater[J],1999,11:253 |
| [3] | Man S.Nature[J],1998,332:119 |
| [4] | Clarkson J R,Price T J,Adams C J.J Chem Soc Faraday Trans[J],1992,88:243 |
| [5] | Brecevic L.J Chem Soc Faraday,Trans[J],1996,92:1 017 |
| [6] | Lopezmacipe A.J Crystal Growth[J],1996,166:1 015 |
| [7] | Falini G,Albeck S,Weiner S,et al.Science[J],1996,271:67 |
| [8] | Naka K,Tanaka Y,Chujo Y,et al.Chem Commun[J],1999:1 931 |
| [9] | kawaguchi H,Hirai H,Sakai K,et al.Colloid Polym Sci[J],1992,270:1 176 |
| [10] | Naka K,Keum D K,Tanaka Y,et al.Chem Commun[J],2000:1 537 |
| [11] | Andersen F.Brecevic A L.Acta Chem Scandinavica[J],1991,45:1 018 |
| [12] | Beniash E,Aizenberg J,Addadi L,et al.Proc Soc London Ser B[J],1997,264:461 |
| [13] | Kontoyannis C G,Vagenas N V.Analyst,2000,125:251 |
| [14] | JIANG Lu-Hua(姜鲁华),DU Fang-Lin(杜芳林),ZHANG Zhi(张志).China Powder Sci Tech(中国粉体技术)[J],2002,8(5):31 |
| [15] | NIE Qiu-Lin(聂秋林),ZHENG Yi-Fan(郑遗凡),YUE Lin-Hai(岳林海),et al.Chinese J Inorg Chem(无机化学学报)[J],2003,19(4):445 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%