以Ag片作催化剂在室温下制备了具有较高比表面积(177 m2/g)的电化学电容器材料MnO2.XRD测试和SEM分析表明,所制备的MnO2为纳米纤维组成的仙人球状微球结构的α-MnO2.交流阻抗、循环伏安、恒流充放电和循环寿命等电化学测试均表明,所合成的α-MnO2微球在1 mol/L Na2SO4水溶液中具有良好的电化学电容性能,单电极比电容可达187.1 F/g,经1 000次循环后电极容量仍保持在90%以上.
参考文献
| [1] | Conway B E.Electrochemical Supercapacitors[M] New York:Plenum Publishers,1999 |
| [2] | Zheng J P,Jow R J.J Electrochem Soc[J],1996,62(1):155 |
| [3] | Peter J M,George L P,Sarki M K,Anthony M V.J Power Source[J],2000,91:68 |
| [4] | Zheng J P,Jow T R.J Electrochem Soc[J],1995,142(8):2 699 |
| [5] | Conway B E.J Electrochem Soc[J],1991,138(6):1 539 |
| [6] | Wang Y G,Xia Y Y.Electrochim Acta[J],2006,51(16):3 223 |
| [7] | Zhang F B,Zhou Y K,Li H L.Mater Chem Phys[J],2004,83:260 |
| [8] | ZHANG Mi-Lin(张密林),YANG Chen(杨晨),CHEN Ye(陈野),XUE Yun(薛云).Chinese J Power Sources(电源技术)[J],2004,28(10):626 |
| [9] | LIU Xian-Ming(刘献明),ZHANG Xiao-Gang(张校刚).Chinese J Inorg Mater(无机材料学报)[J],2003,18(5):1 022 |
| [10] | Reddy R N,Reddy R G.J Power Sources[J],2004,132:315 |
| [11] | Subramanian V,Zhu H W,Vajtai R,Ajayan P M,Wei B Q.J Phy Chem B[J],2005,109:20 207 |
| [12] | Xiao F,Zhang X G,Hu F P,Zhang J L.Mater Chem Phys[J],2005,94:221 |
| [13] | YUAN Chang-Zhou(原长洲),ZHANG Xiao-Gang(张校刚),GAO Bo(高博).Chinese J Appl Chem(应用化学)[J],2006,23(4):456 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%