采用甘氨酸-硝酸盐法合成了La2CuO4复合氧化物,并制成厚膜型氧敏元件.结果表明,在400～700 ℃之间,厚膜型La2CuO4的灵敏度随着测试温度的升高而逐渐降低.La2 CuO4气敏元件的灵敏度(RN2/Ro2)主要由表面载流子浓度决定,随着测试温度的升高,吸附氧在粒子表面的脱附速率增大,导致空穴载流子浓度随温度的升高而降低,从而使灵敏度下降.厚膜型La2CuO4在400℃时的灵敏度最大,可以达到29.6,远大于烧结型La2CuO4的灵敏度,且厚膜型La2CuO4在400℃对于氧分压变化具有快速的响应,响应时间约为4 s.
参考文献
| [1] | JIAN Jia-Wen (简家文),YANG Bang-Chao (杨邦朝),ZHANG Yi-Kang (张益康).Transducer and Mitrosystem Ttech (传感器技术)[J],2002,21(3):55 |
| [2] | XU Yan-Ji(徐艳姬),XU Ming-Xia(徐明霞),XIE Shao-Qiao(谢少桥),LI Yan(李岩),XU Ting-Xian(徐廷献).Rare Metal Mater Eng(稀有金属材料与工程)[J],2005,34 (5):709 |
| [3] | Kondo H,Takahashi H,Takeuchi T,Igarashi I.In Proc 3rd Sensor Symp,Japan,1983:185 |
| [4] | HOU Feng(侯峰),XU Ting-Xian(徐廷献),YIN Yu-Xin(阴育新),XU Ming-Xia(徐明霞).J Chinese Ceram Soc(硅酸盐学报)[J],2001,29(4):381 |
| [5] | HOU Feng(侯峰),XU Ting-Xian(徐廷献),QIN Yong-Ning(秦永宁).J Ceramics(陶瓷学报)[J],2004,25(1):11 |
| [6] | LI Xiao-Lei(李晓雷),XU Ting-Xian(徐廷献).Chinese Ceram(中国陶瓷),2003,39(1):15 |
| [7] | Nozaki H,Tanaka J.Jpn J Appl Phys[J],1987,26:L1 881 |
| [8] | Zakrzewska K.Thin Solid Films[J],2001,391:229 |
| [9] | HE Jun(何俊),SUN Ying-Jia(孙颖稼),LI Hong(李红).J Mol Catal(分子催化)[J],1994,8(5):325 |
| [10] | WANG Chun-Xiu(王春秀),LI Fu-Li(李福利).Spectrosc Spect Anal(光谱光与光谱分析),2006,26(5):846 |
| [11] | CAO Xue-Qiang(曹学强),ZHONG Zi-Yi(钟子宜),ZENG Yue(曾跃).Acta Sci Nat Univ Norm Hu Nan(湖南师范大学自然科学学报)[J],1997,20(4):45 |
| [12] | LIU Shi-Ming(刘石明),XING Chang-Sheng(邢长生),QIAN Xiao-Liang(钱晓良).J Huazhong Univ Sci Technol(Nat Sci Edn) (华中科技大学学报(自然科学版))[J],2005,33(1):81 |
| [13] | ZHAO Zhen(赵震),YANG Xiang-Guang(杨向光),WU Yue(吴越).J Rare Earth(中国稀土)[J],2003,21(z2):35 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%