采用甘氨酸-硝酸盐法(GNP)合成了单相的钙钛矿结构Sm1-xSrxCrO3(0≤x≤0.1),并进行了XRD、SEM、直流电导率及电化学复阻抗分析测试. 结果表明,Sm1-xSrxCrO3为p型半导体,体系电导率随着锶掺杂量的增加而增大. Sm1-xSrxCrO3在很宽的氧分压范围和高温水蒸汽条件下表现出良好的化学稳定性. Sm0.9Sr0.1CrO3/YSZ(SSCO1/YSZ)复合阳极在CH4和O2 混合气氛中表现出较好的催化性能. YSZ的质量分数为23%的复合电极在800 ℃的CH4+O2混合气氛中得到的最小极化电阻为3.24 Ω·cm2.
参考文献
| [1] | He H P,Huang Y Y,Vohs J M,Gorte R J.Solid State Ionics[J],2004,175:171 |
| [2] | Jiang S P,Chan S H.J Mater Sci[J],2004,39:4 405 |
| [3] | Koh J H,Yoo Y S,Park J W,Lim H C.Solid State Ionics[J],2002,149:157 |
| [4] | Minh N Q.J Am Ceram Soc[J],1993,76(3):563 |
| [5] | Lu C,Worrell W L,Vohs J M,Gorte R J.J Electrochem Soc[J],2003,150(3):A354 |
| [6] | Jiang S P,Chen X J,Chan S H,Kwok J T,Khor K A.Solid State Ionics[J],2006,177:149 |
| [7] | Hirota K,Io M,Hatta H,Yoshinaka M,Yamaguchi O.J Solid State Chem[J],2003,174:80 |
| [8] | Hirota K,Hatta H,Io M,Yoshinaka M,Yamaguchi O.J Mater Sci[J],2003,38:3 431 |
| [9] | Sundaram R,Raj E S,Nagaraja K S.Sensors and Actuators[J],2004,B99:350 |
| [10] | Brown I D.Acta Cryst[J],1992,B48:553 |
| [11] | Jiang S P.J Electrochem Soc[J],2003,150(11):548 |
| [12] | LI Qiang(李强),FAN Yong(范勇),ZHAO Hui(赵辉),HUO Li-Hua(霍丽华).Chinese J Inorg Chem(无机化学学报)[J],2006,22(11):2 025 |
| [13] | Hagiwara A,Hobara N,Takizawa K,Sato K,Abe H,Naito M.Solid State Ionics[J],2006,177:2 967 |
| [14] | Kuo C H,Gupta P K.Acta Metall Mater[J],1995,43:397 |
| [15] | Wüthrich R,Bleuler H.Electrochim Acta[J],2004,49:1 547 |
| [16] | Napporn T W,Jacques-Bédard X,Morin F,Meunier M.J Electrochem Soc[J],2004,151(12):A2 088 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%