采用钯催化的Suzuki偶合方法合成了一系列9,9-二辛基芴(DOF)和4,7-二噻吩-2,1,3-苯并硒二唑的红光共聚物PFO-BTSe. 当在聚芴主链中引入4,7-二噻吩-2,1,3-苯并硒二唑后,其发光波长发生红移,最大发光波长由PFO-BTSe0.1时的669 nm红移至PFO-BTSe35时的727 nm. 当BTSe的摩尔分数为0.5%时,芴链段在420 nm左右的发光已完全被淬灭,其能量已完全转移到BTSe单元. 由这些聚合物所制得的器件最大外量子效率为1.24%,亮度为83 cd/m2,对应的BTSe单元的摩尔分数为0.1%.
参考文献
| [1] | Tang C W,Vanslyke S A.Appl Phys Lett[J],1987,51:913 |
| [2] | Blondin P,Bouchard J,Beaupr S,Bellet te M,Durocher G,Leclerc M.Macromolecules[J],2000,33:5 874 |
| [3] | Chen Z K,Huang W,Wang L H,Kang E T,Chen B J,Lee C S.Macromolecules[J],2000,33:9 015 |
| [4] | Hou Q,Xu Y S,Yang W.J Mater Chem[J],2002,12:2 887 |
| [5] | Mazzeo M,Vitale V,Della Sala F,Pisignano D,Barbarella G,Favaretto L,Zanelli A,Cingolani R,Gigli G.Adv Mater[J],2003,15:2 060 |
| [6] | Morin J F,Leclerc M.Macromolecules[J],2002,35:8 413 |
| [7] | Liu J,Min C C,Zhou Q G l.Appl Phys Lett[J],2006,88(8):083 505 |
| [8] | Zhang H X,Li Y,Jiang Q.J Mater Sci[J],2007,42:4 476 |
| [9] | Cao D R,Liu Q L,Zeng W J,Han S H,Peng J B,Liu S P.J Polym Sci,Part A(Polym Chem)[J],2006,44(8):2 395 |
| [10] | Lee Y D,Chen C T,Chan L H.Org Electronics[J],2006,7(1):55 |
| [11] | Peng Q,Kang E T,Neoh K G,Xiao D,Zou D C.J Mater Chem[J],2006,16(4):376 |
| [12] | Chen M X,Berggren M,Perzon E,Robisson N,Jonsson S K M,Andersson M R,Fahlman M.Synth Met[J],2004,146(3):233 |
| [13] | Ranger M,Rondeau D,Leclerc M.Macromolecules[J],1997,30:7 686 |
| [14] | Pinhey J T,Roche E G.J Chem Soc,Perkin,Trans 1[J],1988:2 415 |
| [15] | Bird C W,Cheeseman G W H,Sarsfield A A.J Chem Soc[J],1963:4 767 |
| [16] | Kitamura C,Tanaka S,Yamashita Y.Chem Mater[J],1996,8:570 |
| [17] | Inbasekaran M,Woo E P,Wu W S,Bernius M T.W0 046 321A1[P],2000 |
| [18] | Leeuw D M,Simenon M M J,Brown A R,Einerhand R E F.Synth Met[J],1997,87:53 |
| [19] | Tu G L,Zhou Q G,Cheng Y X,Wang L X,Ma D G,Jing X B,Wang F S.Appl Phys Lett[J],2004,85(12):2 172 |
| [20] | Luo J,Li X Z,Hou Q,Peng J B,Yang W,Cao Y.Adv Mater[J],2007,19:1 113 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%