用失重法、电化学法和原子力显微镜(AFM)研究了红四氮唑在1.0～5.0 mol/L HCl介质中对冷轧钢的缓蚀作用. 结果表明,红四氮唑对冷轧钢具有良好的缓蚀作用,为混合抑制型缓蚀剂,且在钢表面的吸附符合Langmuir吸附模型. 通过吸附热力学和动力学参数讨论了缓蚀作用机理. AFM测试结果表明,红四氮唑在钢表面吸附形成了致密的缓蚀剂膜层.
参考文献
| [1] | Li X H,Mu G N.Appl Surf Sci[J],2005,252:1 254 |
| [2] | Bentiss F,Traisnel M,Gengembre L,Lagrenée M.Appl Surf Sci[J],2000,161:194 |
| [3] | Abdennaby A M S,Abdulhady A I,Abu-Oribi S T,Saricimen H.Corros Sci[J],1996,38:1 791 |
| [4] | Quraishi M A,Hariom K.Mater Chem Phys[J],2002,78:18 |
| [5] | HE Qiao(何桥),ZHANG Sheng-Tao(张胜涛),LI Wei-Hua(李伟华),PEI Chang-Ling (裴长岭),HOU Bao-Rong (侯保荣).Corros Protect(腐蚀与防护)[J],2008,29:243 |
| [6] | Kertit S,Hammouti B.Appl Surf Sci[J],1996,93:59 |
| [7] | Morales-Gil P,Negrón-Silva G,Romero-Romoa M,ngeles-Chávez C,Palomar-Pardavé M.Electrochim Acta[J],2004,49:4 733 |
| [8] | LI Rong(李容),HE Xiao-Ying(何晓英),LI Ming-Qi(李明齐),LIAO Fang(廖钫).J China West Normal Univ(西华师范大学学报)[J],2005,26(4):410 |
| [9] | Li X H,Deng S D,Mu G N,Fu H,Yang F Z.Corros Sci[J],2008,50:420 |
| [10] | MU Guan-Nan(木冠南),LI Xiang-Hong(李向红),QU Qing(屈庆),ZHOU Jun(周俊).J Chem Ind Eng(化工学报)[J],2005,56(11):2 150 |
| [11] | Sekine I,Hirakawa Y.Corrosion[J],1986,42(5):272 |
| [12] | Ashassi-sorkhabi H,Majidi M R,Seyyedi K.Appl Surf Sci[J],2004,225:176 |
| [13] | Mathur P B,Vasudevan T.Corrosion[J],1982,38(3):171 |
| [14] | CAO Chu-Nan(曹楚南).Corrosion Electrochemistry Mechanism(腐蚀电化学原理)[M].Beijing(北京):Chemical Industrial Engineering Press(化学工业出版社),2004:235 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%