以1,4-二苯氧基苯为单体分别与N,N'-(4,4'-二苯甲烷)-双-(3,4-二甲酰亚胺基苯甲酰氯)和N,N'-(4,4'-二苯砜)-双-(3,4-二甲酰亚胺基苯甲酰氯),采用低温溶液缩聚合成了2种主链含酰亚胺结构的聚醚醚酮树脂,聚合物的比浓对数粘度分别为0.98和0.61 dL/g. 用FT-IR、~1H NMR和WAXD进行了结构表征,用DSC和TGA测试了热性能. 结果表明,聚合物有较高的玻璃化转变温度(T_g分别为236和263 ℃),N2气气氛中热分解温度(5% T_d)分别为529和512 ℃,能溶于N,N-二甲基乙酰胺、N-甲基-2-吡咯烷酮、氯仿和间甲酚等常见的有机溶剂中.
Two novel poly ( ether ether ketone ) s ( PEEK ) containing imide moiety with inherent viscosities of 0. 98 dL/g and 0. 61 dL/g were respectively prepared by low temperature solution polycondensation from 1,4-diphenylbenzene( DPB) with N,N'-(4,4'-diphenylmethane) bistrimelletimide diacid chloride( DCDI-M) or N,N'-(4,4'-diphenylsulfone) bistrimelletimide diacid chloride( DCDI-S). The polymers were characterized by FT-IR, ~1H NMR, DSC, TGA and WAXD. The results show that the polymers are amorphous. The glass transition temperatures( T_g) are 236 ℃ and 263 ℃ , respectively. The onset temperatures taken at a 5% mass loss of each of the polymers in nitrogen atmosphere are all over 512 ℃. The polymers are soluble in common organic solvents such as N, N-dimethylacetamide ( DMAc) , TV-methylpyrrolidone (NMP), cresol and chloroform at room temperature.
参考文献
| [1] | Harris J E,Winslow P A,Botkin J H,Maresca L M,Clendinning R A,Cotter R J,Matzner M,Kwiatkowski G T.Macromolecules[J],1993,26(9):2 366 |
| [2] | Wang F,Roovers J.Macromolecules[J],1993,26(20):5 295 |
| [3] | TONG Yong-Fen(童永芬),SONG Cai-Sheng(宋才生),CHEN Lie(谌烈),WEN Hong-Li(温红丽),LIU Xiao-Ling(刘晓玲).Chinese J Appl Chem(应用化学)[J],2004,21(10):993 |
| [4] | Cao J K,Su W C,Wu Z W,Kitayama T,Hatada K.Polymer[J],1994,35(16):3 549 |
| [5] | Ding F C,Wang S J,Xiao M,Han D M,Meng Y Z.Polym Sci[J],2007,106(3):1 821 |
| [6] | DANG Guo-Dong(党国栋),ZHOU Hong-Wei(周宏伟),YANG Wei(杨薇),CHEN Chun-Hai(陈春海),WU Zhong-Wen(吴忠文),LI Fei(李菲).Chem J Chinese Univ(高等学校化学学报)[J],2005,26(1):166 |
| [7] | JIAN Xi-Gao(蹇锡高),CHEN Ping(陈平),LIAO Gong-Xiong(廖功雄),ZHU Xiu-Lin(朱秀林),ZHANG Shou-Hai(张守海),WANG Jin-Yan(王锦艳).Acta Polym Sin(高分子学报)[J],2003,(4):469 |
| [8] | CHEN Xiao-Ting(陈晓婷),SUN Hao(孙皓),TANG Xu-Dong(唐旭东),WANG Chun-Ying (王春颖).Chem J Chinese Univ(高等学校化学学报)[J],2007,28(5):999 |
| [9] | Fitch J W,Reddy V S,Youngman P W.Polymer[J],2000,41(6):2 301 |
| [10] | Patrick J H,Richard H W.J Mater Chem[J],1991,1(2):271 |
| [11] | Matsuo S,Mitsuhashi K I.J Polym Sci:Part A Polym Chem[J],1994,32:1 969 |
| [12] | Frank W M,Martin T M,Gloria M,Matilda M.Polym Sci[J],1995,56(11):1 397 |
| [13] | LIU Yong-Jun(刘勇军),SONG Cai-Sheng(宋才生),FU Chang-Qing(付长清),YE Shang-Hui(叶尚辉).Polym Mater Sci Eng(高分子材料科学与工程)[J],2005,21(6):98 |
| [14] | ZHONG Ming(钟鸣),XU Ling(徐玲),SONG Cai-Sheng(宋才生),DAI Run-Ying(戴润英),HUANG Hong(黄红).Acta Polym Sin(高分子学报)[J],2008,(6):616 |
| [15] | SONG Cai-Sheng(宋才生),CAI Ming-Zhong(蔡明中),ZHOU Li-Yun(周丽云).Acta Polym Sin(高分子学报)[J],1995,(1):99 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%