本文报道La0.825Sr0.175MnO3掺Cu样品的电磁特性.在一定掺杂量情况下,样品的电阻率随温度出现双峰现象,该现象不能用与晶粒尺寸有关的模型来解释,从直流磁化率结果看,样品中存在大量无规取向的铁磁团蔟可能是电阻率双峰出现的根本原因.
参考文献
| [1] | R Von Hemolt et al.[J].Solid State Communications,1992,82:693. |
| [2] | N F Mott .[J].Advances in Physics,1972,21:785. |
| [3] | J W Cai et al.[J].Applied Physics Letters,1997,71:1727. |
| [4] | A. Barman;M. Ghosh;S. Biswas .Giant magnetoresistance in La↓(0.8)Sr↓(0.2)Fe↓(x)Co↓(1-x)O↓(3)(0.025≤X≤0.3)[J].Applied physics letters,1997(21/24):3150-3152. |
| [5] | Y Sun et al.[J].Physical Review B,1999,60:12317. |
| [6] | D Emin;Holstein .[J].Ann Phys Rev B,1976,13:647. |
| [7] | E O Wollan;W C Koehler .[J].Physical Review,1955,100:545. |
| [8] | J B Goodenough;A L Loeb .[J].Physical Review,1955,98:391. |
| [9] | J. R. Sun;G. H. Rao;Y. Z. Zhang .Effects of inhomogeneous oxygen content in (La,Gd)↓(0.7)Ca↓(0.3)MnO↓(3+δ) perovskites[J].Applied physics letters,1998(24/26):3208-3210. |
| [10] | 郑磊 .[D].博士学位论文,1999. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%