采用Nd0.7Sr0.3MnO3/SrTiO3/YBa2Cu3O7-δ的异质结构,研究了自旋极化准粒子的注入效应.在56μm宽的YBCO膜条上成功地制备了与超导膜条同样宽度但不同长度的六个注入结区,长度L分别为80μm, 40μm, 20μm, 10μm, 5μm和2μm.80nm厚的YBCO薄膜在16K温度下Jc为2×105A/cm2.Iin=0.5mA的自旋电流注入下,随L从80μm逐渐顺次减小时,注入效率η=ΔJc/ΔJin逐渐增大.而当L≤20μm后,η不再增加,达到几乎相同的值(~6).初步分析认为这与自旋极化准粒子在超导膜内的有效自旋扩散长度有关.异质结构中YBCO薄膜的超导电性以及注入窗口的尺寸对获得大的自旋注入效率十分重要.
参考文献
[1] | A J Millis .[J].Nature,1998,392:147. |
[2] | V A Vas′ko;V A Larkin;P A Kraus;K R Nikolaev D E Grupp C A Nordman A M Goldman .[J].Physical Review Letters,1997,78:1134. |
[3] | Z. W. Dong;R. Ramesh;T. Venkatesan .Spin-polarized quasiparticle injection devices using Au/YBa↓(2)Cu↓(3)O↓(7)/LaAlO↓(3)/Nd↓(0.7)Sr↓(0.3)MnO↓(3) heterostructures[J].Applied physics letters,1997(9/12):1718-1720. |
[4] | N-C Yeh;R P Vasquez;C -C Fu;A V Samoilov Y Li K Vakili .[J].Physical Review B,1999,60:10522. |
[5] | R M Stroud;J Kim;C R Eddy;D B Chrisey J S Horwitz D Koller M S Osofsky R J Soulen R C Y Auyeung .[J].Journal of Applied Physics,1998,83:7189. |
[6] | Y Gim A W Kleinsasser;J B Barner .[J].Journal of Applied Physics,2001,90:4063. |
[7] | C-C Fu;Z Huang;N -C Yeh .[J].Physical Review,2002,B65:224516. |
[8] | 杨名,崔旭高,杨森祖,张世远,康琳,吉争鸣,许伟伟,吴培亨.添加Ag的Nd0.7Sr0.3MnO3薄膜研究[J].低温物理学报,2002(04):248-253. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%