本文报道了利用化学气相沉积技术制备MgB2超导薄膜.首先在MgO(111)基片上化学气相沉积一层B膜,然后在Mg蒸气环境下对B膜进行后退火处理.退火后得到的MgB2薄膜在MgO(111)基片上呈随即取向生长,Mg、B原子比接近于1∶2.4;薄膜表面光滑致密,晶粒粒度约为0.5μm.电阻测量和直流磁测量表明薄膜超导转变温度为38K,转变宽度仅为0.1K.毕恩公式计算结果显示MgB2薄膜的临界电流密度在0T、10K时高达2×107A/cm2.
参考文献
| [1] | Jun Nagamatsu et al.[J].Nature,2001,410:63. |
| [2] | Jin S et al.[J].Nature,2001,411:563. |
| [3] | Bugoslavsky Y et al.[J].Nature,2001,411:561. |
| [4] | Berenov A et al.[J].Applied Physics Letters,2001(79):4001. |
| [5] | Brinkman A.;Rijnders G.;Leca V.;Smilde HJH.;Oomen I. Golubov AA.;Roesthuis F.;Harkema S.;Hilgenkamp H.;Blank DHA.;Rogalla H.;Mijatovic D. .Superconducting thin films of MgB2 on Si by pulsed laser deposition[J].Physica, C. Superconductivity and its applications,2001(1/2):1-4. |
| [6] | Ermolov SN.;Rossolenko AN.;Bdikin IK.;Uspenskaya LS. Stepakov NS.;Glebovskii VG.;Indenbom MV. .Superconducting MgB2 films obtained by magnetron sputtering[J].JETP Letters,2001(10):557-561. |
| [7] | Kenji Ueda;Michio Naito .As-grown superconducting MgB_(2) thin films prepared by molecular beam epitaxy[J].Applied physics letters,2001(13):2046-2048. |
| [8] | Paranthaman M et al.[J].Applied Physics Letters,2001(78):3669. |
| [9] | ZENG X H;Pogrebnyakov A V;Kotcharov A et al.[J].Nature Materials,2002,1(01):1. |
| [10] | Fu X H;Wang D S;Zhang Z P et al.[J].PHYSICA C,2002,377:407. |
| [11] | Wang Shu-Fang;Zhou Yue-Liang;Zhu Ya Bin.[J].中国物理快报(英文版),2003 |
| [12] | Ferdeghini C;Ferrando V;Grassano G et al.[J].Superconductor Science and Technology,2001(14):952. |
| [13] | Hyeong-Jin Kim;W N Kang;Eun-Mi Choi 等.[J].Physical Review Letters,2001,87:87002. |
| [14] | C B Eom;M K Lee;J H Choi et al.[J].Nature,2001,411:558. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%