研究了Al和Sn离子掺杂对层状钙钛矿结构锰氧化物La1.2Ca1.8Mn2O7输运性质的影响.发现Al,Sn掺杂后样品电阻率增加,并且半导体导电区域电阻值与可变程跃迁导电模型符合得较好;同时掺杂样品金属-绝缘转变温度逐步降低,最大磁电阻值比未掺杂样品增大.
参考文献
[1] | S Jin;THTiefel;M McCormack et al.[J].Science,1994,264:413. |
[2] | Yukitoshi Motome;NobuoFurukawa;NaotoNagaosa .[J].Physical Review Letters,2003,91:167204. |
[3] | Hirofumi Hazama;TerutakaGoto;Yuichi Nemoto et al.[J].Physical Review B,2004,69:060406. |
[4] | Y Moritomo;AAsamitsu;H Kuwahara et al.[J].Nature,1996,380:141. |
[5] | M Kubota;YOohara;H Yoshizawa et al.[J].Physical Review Letters,2003,91:047201. |
[6] | A Koizumi;TNagao;Y Kakutani et al.[J].Physical Review B,2004,69:060401. |
[7] | H Asano;JHayakawa;M Matsui .[J].Physical Review B,1998,57:1052. |
[8] | K Ghosh;SBOgale;R Ramesh et al.[J].Physical Review B,1999,59:533. |
[9] | Nori Sudhakar;KPRajeevand;AKNigam .[J].Journal of Applied Physics,2003,93:8331. |
[10] | S M Yusuf;MSahana;K Drr et al.[J].Physical Review B,2002,66:064414. |
[11] | Subhayan Biswas;SandipChatterjee;P Chatterjee et al.[J].Physical Review B,2002,66:214403. |
[12] | N F Mott;E A Davis.Electronic Processes in Non-Crystalline solids[M].Oxford University Press,New York,1979 |
[13] | M Viret;LRanno;J M D Coey .[J].Physical Review B,1997,55:8067. |
[14] | G J Snyder;RHiskes;S DiCarolis et al.[J].Physical Review B,1996,53:14434. |
[15] | R M Kusters;JSingleton;D A Keen .[J].Physical Review B,1989,155:362. |
[16] | 曹强,阮可青,李世燕,陈仙辉,钱国光,曹烈兆.Bi2Sr2Ca1-xPrxCu2Oy和Bi2Sr2Ca1-xYxCu2Oy系列单晶样品输运性质的对照研究[J].低温物理学报,2000(03):168-174. |
[17] | 时亮,张新定,冯双久,李广,孙学峰,李晓光.超导铁磁体RuSr2Gd1.4Ce0.6Cu2O10-δ的输运性质和磁共振研究[J].低温物理学报,2002(01):7-11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%