电泳共沉积了含Ag的YBa2Cu3O7-δ厚膜.共沉积膜中的Ag含量随着原料中Ag量的增加而增加.YBa2Cu3O7-δ与Ag两种粒子吸附质子所带电量之间的关系为 QYBCO=-0.1638QAg+0.1519F.添加剂聚乙二醇消弱了固体粒子之间的静电斥力作用,使膜的表面光滑平整.在Ag基带表面有垂直于基带面的沿a-b面生长织构形成.
参考文献
| [1] | Fujimoto M;Nojima H .[J].Japanese Journal of Applied Physics,1993,32(04):L576. |
| [2] | Nojima H;Shintaku H .[J].Japanese Journal of Applied Physics,1991,30(07):L1166. |
| [3] | Nojima H;Nagata M .[J].Japanese Journal of Applied Physics,1990,29(09):1655. |
| [4] | Soh D H;Shan Y Q .[J].Physica C,2000,337(01):44. |
| [5] | Sato N.;Noto K.;Yoshimoto N.;Yoshizawa M.;Kawachi M. .Effect of particle size reduction on crack formation in electrophoretically deposited YBCO films[J].Physica, C. Superconductivity and its applications,2001(Pt.2):1019-1022. |
| [6] | 单玉桥 .熔融织构YBCO超导电性能的研究与改善[D].东北大学,1996. |
| [7] | 李凤华,赵升升,王珏,樊占国.电泳沉积法制备YBaCuO厚膜工艺的研究[J].低温与超导,2003(02):26-28,32. |
| [8] | Yang M;Goringe M .[J].Superconductor Science and Technology,1994,7(06):378. |
| [9] | Fan Z G;Shan Y Q .[J].Physica C,1997,282-287:495-496. |
| [10] | 张正平,王殿生,傅兴华,杨健.低激光能流沉积高质量的NdB2Cu3O7-x/YBa2Cu3O7-y高温超导薄膜[J].低温物理学报,2001(03):167-173. |
| [11] | 王小平,刘援,王霈文,李季,林晨光,华志强,冯稷,吴柏枚,杜英磊.不同衬底上制备YBa2Cu3O7-δ超导薄膜的微结构研究[J].低温物理学报,2002(02):81-86. |
| [12] | 张芹,朱亚彬,王淑芳,路庆凤,周岳亮.利用电泳技术在不锈钢和铁基底上制备MgB2带材[J].低温物理学报,2003(02):137-140. |
| [13] | 李青 .[J].电镀与涂饰,1997,16(04):43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%