我们研究了Tl-2212超导薄膜在带有YSZ/CeO2缓冲层和带有CeO2/YSZ/CeO2缓冲层的Ni金属RABiTS基带上的生长情况.基带上的缓冲层是采用PLD方法制备的,Tl-2212薄膜的制备采用了磁控溅射和后热处理两步方法.XRD 实验结果表明,Tl-2212薄膜都具有很好的c轴垂直于膜面的织构,并具有双向外延生长特性.在CeO2/YSZ/CeO2/Ni基带上制作的Tl-2212薄膜的Tc达到102.8 K,Jc(77K,0T)达到2.6 MA/cm2;在YSZ/CeO2/Ni基带上薄膜的Tc可达97.7K,Jc (77K,0T)也可以达到0.45MA/cm2.
参考文献
| [1] | A Goyal et al.Recent progress in the fabrication of high-Jc tapes by epitaxial deposition of YBCO on RABiTS[J].Physica C,2003,357-360:903. |
| [2] | Jian Yang et al.Epitaxial YSZ/CeO2,YBCO on cube textured nickel[J].Physica C,2000,337:67. |
| [3] | S Kreiskott et al.High Jc YBCO films on biaxially textured Ni with oxide buffer layers deposited using evaporation,sputtering techniques[J].Physica C,2003,383:306. |
| [4] | E D Specht et al.Uniform texture in meter-long YB2C3O7 tape[J].PHYSICA C,2002,382:342. |
| [5] | J Eickemeyer et al.Highly cube textured Ni-W-RABiTS tapes for YBCO coated conductors[J].Physica C,2002,814:372-376. |
| [6] | V. Subramanya Sarma;B. de Boer;J. Eickemeyer .On the development of high strength and bi-axially textured Ni-3 percent W/Ni-10 percent Cr-1.5 percent Al composite substrate for coated conductor application[J].Scripta materialia,2003(8):1167-1171. |
| [7] | S L Yan et al..Formation of epitaxial Tl2Ba2CaCu2O8 thin films at low temperature in pure argon[J].Applied Physics Letters,1993,63:1845. |
| [8] | S Donet et al.YBCO films on buffered Ni RABTiS substrates by pulsed injection MOCVD[J].Physica C,2002,372-376:652. |
| [9] | T C Shields et al..Deposition of YBCO films by high temperature spray pyrolysis[J].Physica C,2002,747:372-376. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%