用真空三源热共蒸发法制备了二十厘米长的涂层导体,其宽度为1厘米, 超导层宽度为0.9 厘米,厚度为600纳米.使用直流四引线法测试,导体在77K时的临界电流大于120安培,相应的临界电流密度大于每平方厘米220万安培.表征电流-电压曲线超导转变陡峭度的n值为35.显微结构观察表明其膜层显微形貌与单晶衬底上的薄膜极其相似.X射线衍射研究表明超导薄膜的相成分纯,面内FWHM为Δφ=6.23°,面外FWHM为Δω=3.84°,表明涂层的优良织构.在此文章将详细报告导体的制备和显微结构及物理测试结果.
参考文献
[1] | Usoskin A;Dzick J;Issaev A;Knoke J ,Garcia-Moreno F ,Sturm K,Freyhardt H C .[J].Superconductor Science and Technology,2001,14:676. |
[2] | Mastsumoto K;Kim S B;Hirabayyashi I;Watanabe T ,Uno N,Ikeda M .[J].Physica C,2000,330:150. |
[3] | Iijinma Y;Kakimoto K;Kimura M;Takeda K .[J].PHYSICA C,2000,335:15. |
[4] | Iijinma Y;Kakimoto K;Kimura M;Takeda K,Satoh T .[J].IEEE Transactions on Applied Superconductivity,2001,11:2816. |
[5] | Lorenz M.;Hochmuth H.;Natusch D.;Grundmann M. .High-quality reproducible PLD Y-Ba-Cu-O: Ag thin films up to 4 inch diameter for microwave applications[J].Physica, C. Superconductivity and its applications,2002(Pt.2):587-589. |
[6] | Utz B.;Semerad R.;Bauer M.;Prusseit W.;Berberich P.;Kinder H. .Deposition of YBCO and NBCO films on areas of 9 inches in diameter[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,1997(2):1272-1277. |
[7] | Knauf J.;Semerad R.;Prusseit W.;DeBoer B.;Eickemeyer J. .YBaCuO-deposition on metal tape substrates[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,2001(1):2885-2888. |
[8] | Prusseit W;Furtner S;Nemetschek R .[J].Superconductor Science and Technology,2000,13:519. |
[9] | Yamane H;Hirait;Watanabe K;Kobayashi N ,Muto Y ,Hasei M,Kurosawa H .[J].Journal of Applied Physics,1991,69:7948. |
[10] | Kurosaki H;Yuasa T;Maeda T;Yamada Y,Kim S B,Watanabe t,Wada K Hirabayashi I .[J].Physica C,2001,938:357-360. |
[11] | Yamada Y.;Suga T.;Hirabayashi I. .Low-temperature growth conditions of YBa2Cu3O7-delta using Ba-Cu-Ag-O-F solvent[J].Journal of Crystal Growth,2002(1/3):221-224. |
[12] | Araki T;Yamagiwa K;Hirabayashi I et al.[J].Superconductor Science and Technology,2001,14:L21. |
[13] | Malozemoff A.[M].Second Generation HTS Wire:An Assessment,2004 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%