我们对多晶样品Nd0.7Sr0.3Mn1-xCrxO3(x≤0.30)进行了X射线衍射谱、电阻温度关系和磁化强度测量.实验发现:随Cr掺杂量的增加,样品的电阻率变大,电阻峰温度和居里温度降低,这是由Cr的介入弱化了双交换作用所致;在x=0.10附近,电阻出现了双峰现象,在其M~T上没有发现与低温峰对应的磁性异常;在锰位磁矩与Cr含量的关系中发现,Cr掺杂对样品的磁性几乎无贡献;通过分析,我们用相分离的图象解释了有关的现象.
参考文献
[1] | M B Salamon;MM Jaime .[J].Reviews of Modern Physics,2001,73:583. |
[2] | C Zener .[J].Physical Review,1951,82:403. |
[3] | Zhou JS.;Goodenough JB. .Phonon-assisted double exchange in perovskite manganites[J].Physical review letters,1998(12):2665-2668. |
[4] | K Ghosh;S B Ogale et al.[J].Physical Review B,1999,59:533. |
[5] | Hajung Song;Woojin Kim et al.[J].Journal of Applied Physics,2001,89:3398. |
[6] | O Cabeza;M Long et al.[J].Journal of Physics:Condensed Matter,1999,11:2568. |
[7] | Y Sun;X j Xu;Y h Zhang .[J].Physical Review B,2000,63:54404. |
[8] | 刘宁,张裕恒,孙勇,童伟.La0.67Ca0.33Mn1-xCrxO3(0.0≤x≤0.15)中异常的CMR效应[J].低温物理学报,2001(02):115-120. |
[9] | E Dagotto et al.[J].Physics Reports,2001,344:1-153. |
[10] | L.F. Cohen;P. S. I. P. N. de Silva;N. Malde .Reentrant metal-insulator-type transition induced by high fluence chromium ion implantation of La↓(0.7)Ca↓(03)MnO↓(3) thin films[J].Applied physics letters,1998(7/12):1005-1007. |
[11] | FANG Jun,TIAN Jian-jun,WANG Fang,SONG Wen-Hai,HUANG Zhen,CHEN Jing-lin.Deoxygenation Enhanced Double-Resistivity-Peak Properties in Polycrystalline La0.7Ca0.3Mn0.92Cr0.08O3-δ[J].中国物理快报(英文版),2004(10):2022-2025. |
[12] | S L Ye;W H Song et al.[J].Journal of Magnetism and Magnetic Materials,2002,248:26. |
[13] | WU Bai-Mei,M. Ausloos,DU Ying-Lei,ZHENG Wei-Hua,LI Bo,J. F. Fagnard,Ph. Vanderbemden.Spin Glass Behaviour and Spin-Dependent Scattering in La0.7Ca0.3Mn0.9Cr0.1O3 Perovskites[J].中国物理快报(英文版),2005(03):686-689. |
[14] | R. Mahendiran;A. Maignan;M. Hervieu .Anomalous magnetotransport in Pr_(0.5)Ca_(0.5)Mn_(0.99)Cr_(0.01)O_(3)[J].Applied physics letters,2000(10):1517-1519. |
[15] | 田建军,方军,王芳,黄真,陈治友,陈敬林.降温速率对La0.7Ca0.3Mn1-xCrxO3(x=0.00,0.08)电磁性质的影响[J].低温物理学报,2005(01):74-78. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%