采用不同烧结和后退火工艺制备了自掺杂锰氧化物La0.9MnO3+δ. X射线衍射结果表明,除La0.9MnO3+δ相外,没有其它杂相. 不同磁场下R～T曲线表明,虽然所有样品都有巨磁电阻效应和金属-绝缘体转变,但氧含量对La0.9MnO3+δ的磁电阻特性有十分明显的影响. 随着氧含量的增加,R～T曲线由一个峰变成两个峰再变成一个峰. 我们认为氧含量增加导致了铁磁畴的居里温度发生变化,样品中可能出现相分离.
参考文献
| [1] | S Jin;T H Tiefel;M McCormack;R.A.Fastnacht,R.Ramesh,and L.H.Chen .[J].SIENE,1994,264:413. |
| [2] | E Dagotto;T Hotta;A Moreo .[J].Physics Reports,2001,344(01) |
| [3] | R Ganguly;I K Gopalakrishnan;J V Yakhmi .[J].Journal of Physics:Condensed Matter,2000,12:L719. |
| [4] | Y G Zhao;R C Srivastava;P Fournier;V.Smolyaninova,M.Rajeswari,T.Wu,Z.Y.Li,R.L.Greene,T.Venkatesan .[J].Journal of Mang Mang Mater,2000,220:161. |
| [5] | S. L. Ye;W. H. Song;J. M. Dai;K. Y. Wang;S. G. Wang;J. J. Du;Y. P. Sun;J. Fang;J. L. Chen;B. J. Gao .Large room-temperature magnetoresistance and phase separation in La_(1-x)Na_(x)MnO_(3) with 0.1≤x≤0.3[J].Journal of Applied Physics,2001(6):2943-2948. |
| [6] | P Mandal;S Das .[J].Physical Review,1997,56:15073. |
| [7] | I O Troyanchuk;V A Khomchenko;M Tovar;H.Szymczak,K.Brner .[J].Physical Review Phys Rev,2004,B69:054432. |
| [8] | C Ritter;M R Ibarra;J M De Teresa;P.A.Algarabel,C.Marquina,J.Blasco,J.Garcia,S.Oseroff,S-W.Cheong .[J].Physical Review,1997,B56:8902. |
| [9] | 李琴,傅泽禄,顾大振,Abbas A.Essa,吉争鸣,康琳,冯一军,杨森祖,吴培亨.利用真空退火的界面工程处理方法制备边缘结[J].低温物理学报,2002(01):40-45. |
| [10] | 张玉风 等.[J].低温物理学报,2004,26(01) |
| [11] | 吴克,余增强,张解东,王守证,聂瑞娟,王福仁.电子束蒸发在不同Ar气氛下外退火制备MgB2超导薄膜[J].低温物理学报,2006(03):212-218. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%