用化学方法制备出La2/3Ca1/3MnO3/TE(TE=Cu、Fe和Zn)复合颗粒系统,并通过零场和外加低磁场(0.3 T)下电阻率(ρ)随温度(T)变化关系测量对这些复合系统的输运和低场磁电阻行为进行了比较性研究.相对于纯La2/3Ca1/3MnO3颗粒系统,Cu引入后,绝缘体-金属转变温度(TIM)降低,ρ减小,ρ(T)曲线表现出明显的热滞豫现象,磁电阻(MR)在转变温度附近表现出峰行为且峰值处的MR值高达~35%.引入Fe后,TIM升高,电阻率减小,但MR随T降低而单调增加.引入Zn后,TIM降低,ρ增加,在TIM附近也出现MR峰但峰值较小.同时,也注意到,在含Fe和Zn的系统中都没有观察到明显的热滞豫现象.
参考文献
[1] | R von Helmolt;J Weeker;B Holzapfel;L Schultz,K Samwer .[J].Physical Review Letters,1993,71:2331. |
[2] | S Jin;T H Chen .[J].Science,1994,264:413. |
[3] | J S Helman;B Abeles .[J].Physical Review Letters,1976,37:1429. |
[4] | P Raychaudhuri et al.[J].Physical Review,1999,B59:13919. |
[5] | J. M. D. Coey;A. E. Berkowitz;LI. Balcells .Magnetoresistance of magnetite[J].Applied physics letters,1998(1/6):734-736. |
[6] | F Guinea .[J].Physical Review,1998,B58:9212. |
[7] | J M D Coey;A E Berkowitz;LiBalcells;F F Putris,A Barry .[J].Physical Review Letters,1998,80:3815. |
[8] | L E Hueso;J Rivas;F Rivadulla;M A Lopez-Quintela .[J].Journal of Applied Physics,2001,89:1746. |
[9] | Z C Xia;S L Yuan;F Tu;C Q Tang,G Peng,G Q Zhang,L Liu,J Liu,Z Y Li,Y P Yang,C S Xiong,Y H Xiong .[J].Journal of Physics D:Applied Physics,2002,35:177. |
[10] | 袁松柳;方重华;缪菊红;刘胜,夏正才 .[J].无机材料学报,2005,20:624. |
[11] | G Turilli;F Licci .[J].Physical Review,1996,B54:13052. |
[12] | 朱永文,方军,黄真,高秉钧.(La1-x Yx)0.5Sr0.5MnO3体系的结构和输运性质研究[J].低温物理学报,2003(02):151-156. |
[13] | 刘莉,牛乐园,张力江,夏正才,袁松柳.热处理温度对La4/3Sr5/3Mn2O7的结构及电输运性质的影响[J].低温物理学报,2004(04):295-299. |
[14] | 张力江,刘莉,夏正才,张国宏,冯文,唐洁,刘胜,袁松柳.La4/3(Sr1-xBax)5/3Mn2O7的电输运性质研究[J].低温物理学报,2004(04):304-308. |
[15] | 张国宏,夏正才,袁松柳.La2/3Ca1/3Mn1-xCuxO3(x=4%)中的热弛豫现象[J].低温物理学报,2004(04):309-313. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%