随着超导磁体的不断开发应用,对高临界电流密度超导材料的需求不断增长,以金属间化合物为基体的超导材料Nb3Sn具有特殊的实际意义,其制成的导体临界性能高于NbTi导体,Nb3Sn股线也是ITER磁体的关键组成部分.为了选择超导磁体合适的运行参数以及确定其稳定运行的范围,了解其超导特性是必要的.根据磁体设计所用标准,磁体运行时性能与股线的性能密切相关.本文介绍了一种测试Nb3Sn股线临界性能的方法,实验采用四引线法进行,测试中对样品提供了一个垂直方向的背景磁场,其大小可从0 T变化到16 T,实验时样品置于变温杜瓦内,温度调节通过控制进入变温杜瓦的氦气量来实现,可使温度变化小于0.01 K.对测试结果运用Summer定理进行了拟合并加以分析.
参考文献
| [1] | Jager B Boequillum.[A].,1996:435. |
| [2] | A Martinez;J L Duchateau .[J].CRYOGENICS,1997,37:865. |
| [3] | Arno Godeke;Bennie Ten Haken;Herman H. J. Ten Kate .Toward an accurate scaling relation for the critical current in niobium-tin conductors[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,2002(1):1029-1032. |
| [4] | Arno Godeke;Bennie ten Haken;Herman H. J. ten Kate .Scaling of the critical current in ITER type niobium-tin superconductors in relation to the applied field, temperature and uni-axial applied strain[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,1999(2 Pt.1):161-164. |
| [5] | L T Summers;M W Guinan et al.[J].IEEE Transactions on Magnetics,1991,27:2041. |
| [6] | M Suenaga;K Tsuchiya et al.[J].CRYOGENICS,1985,25:123. |
| [7] | L Zani;D Ciazynski et al.[J].Physica C,2004,401:94. |
| [8] | 王银顺,肖立业,林良真,戴少涛,舒立.银包套Bi2223多芯带材局部临界电流的变化对整个长样带材性能的影响[J].低温物理学报,2002(03):218-223. |
| [9] | 田建军,方军,王芳,黄真,陈治友,陈敬林.降温速率对La0.7Ca0.3Mn1-xCrxO3（x=0.00,0.08）电磁性质的影响[J].低温物理学报,2005(01):74-78. |
| [10] | 李晓航 等.[J].低温物理学报,2006,28:77. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%