采用熔盐法成功制备出了BaPb0.75Bi0.25O3(BPBO)超导体,对其反应机理进行了研究,并对制得样品的晶体结构、形貌及超导电性进行了测试和分析.X射线粉末衍射及磁性测量结果显示,在较高反应温度(500℃和600℃)下制备的样品具有较好的单相性,无杂相,晶体结构属四方晶系.最高的超导转变温度可达11.6 K.
参考文献
[1] | A.W.Sleisht;J.L.Gillson;P.E.Bierstedt .[J].Solid State Communications,1975,17:27. |
[2] | A.Katsui;Y.Hidaka;H.Takagi .[J].Journal of Crystal Growth,1982,66:228. |
[3] | M.Suzuki;Y.Enomoto;T.Murakami;T.Insmura .[J].Journal of Applied Physics,1982,53:1622. |
[4] | T. Nishida;I. Kawakami;M. Norimoto .Preparation of Ba(Pb_(1-x)Bi_x)O_3 electrode thin films by rf magnetron sputtering[J].Ceramics International,2004(7):1089-1093. |
[5] | K.Kakinuma;K.Fueki .[J].Solid State Communications,1998,105:173. |
[6] | Chia-Liang Sun;Hong-wen Wang;Ming-Chu Chang;Meng-Suan Lin.San-Yuan Chen .[J].Materials Chemistry and Physics,2002,78:507. |
[7] | B.Rapp .[J].Materials Today,2005,8:6. |
[8] | 谢刚.熔融盐理论与应用[M].北京:冶金工业出版社,1998:90. |
[9] | P.Afanasiev;C.Geantet .[J].Coordination Chemistry Reviews,1998,178-180:1725. |
[10] | D.H.Kerridge;Rey.J.Cancela .[J].Journal of Inorganic and Nuclear Chemistry,1975,37:975. |
[11] | D.V.Korolkov;G.P.Kogtikova;Y.P.Kostikov .[J].Physica C,2002,383:117. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%