介绍了温压技术的工艺过程和致密化机制,采用温压工艺制备铁基粉末冶金材料,优选出了适合于温压工艺的聚合物添加剂,并确定了其最佳压制温度范围.试验表明,采用温压工艺可提高材料的生坯和烧结体密度以及力学性能.
参考文献
| [1] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1982:381. |
| [2] | Capus J;Pickering S;Weaver A .Hoeganaes offers higher density at lower cost[J].Metal Powder Report,1994,49(7,8):22-24. |
| [3] | Howard G. Rutz;Francis G. Hanejko .HIGH DENSITY PROCESSING OF HIGH PERFORMANCE FERROUS MATERIALS[J].International Journal of Powder Metallurgy,1995(1):9,11-17-0. |
| [4] | 亓家钟 .Ancodense温压工艺[J].粉末冶金工业,1995,5(01):14-16. |
| [5] | QMP looks at high density products[J].Metal Powder Report,1994,49(7,8):23. |
| [6] | 果世驹;李明怡;林涛 等.无粘结剂铁粉的温压工艺研究[J].粉末冶金工业,1996,6(06):5-9. |
| [7] | Luk .Metal powder cmpositions containing binding agents for elevated temperature compaction[P].US:5429792,1995. |
| [8] | Storstrom;Helge;Johansson et al.Metal powder composition for warm compaction and method for producing sintered products[P].US:5744433,1998. |
| [9] | 果世驹 等.粉末烧结钢温压粘结剂玻璃化温度调整的预测方程[J].粉末冶金技术,1997,15(02):85-88. |
| [10] | St-Laurent S;Chagnon F;言小雄 .为温压工艺设计的混合粉[J].粉末冶金技术,1998,16(01):40-51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%