用材料变形的热激活机制研究了16MnR钢断裂韧性在韧脆转变区随温度的变化规律,通过对Peierls能垒双峰模型的分析计算,得出了Peierls能垒形状因子α＝9时16MnR钢断裂韧性J积分随温度的变化规律,并与16MnR钢低温断裂韧性的试验结果进行了比较.结果表明:韧脆转变区16MnR钢断裂韧性双峰的出现是Peierls机制的作用,该工作已在工程上得到了应用.
参考文献
| [1] | 陈南平 .机械工程与材料科学[J].机械工程材料,1994,18(01):7,53. |
| [2] | 秦江阳,王印培,柳曾典,陈进.球形压力容器用钢的断裂韧性与最低使用温度[J].石油机械,2000(03):18-20. |
| [3] | Rice J R;Thomson R .Ductile versus brittle behavior of crystals[J].Philosophical Magazine,1974,29(01):73-97. |
| [4] | Surek T et al.Dislocation glide controlled by linear elastic obstacles: Athermodynamic analysis[J].Philosophical Magazine,1973,27(02):425-440. |
| [5] | 祝东 .BCC金属形变和断裂的热激活本质及其动态屈服与动态断裂的研究[D].北京:钢铁研究总院,1989. |
| [6] | 李广海;吴希俊 .16Mn钢的无延性韧脆转变与位错热激活过程的关系[J].金属学报,1988(24):SAl-SA6. |
| [7] | Dom J E;Rajnak S .Nucleation of kink pairs and the Peierls' mechanism of plastic deformation[J].Transactions of the Metallurgical Society of AIME,1964,230:1052-1064. |
| [8] | Armstrong R W .Relation between the Perch" friction" stress and the thermal activation rate equation[J].Acta Materialia,1967,15(04):667-668. |
| [9] | 吴希俊;姜健;尹花子 .三点弯曲试样J积分和应变能间关系式的试验研究[J].金属学报,1978,14(04):420-429. |
| [10] | 龙期威 .低碳钢的断裂韧性和屈服强度的低温温度依赖性[J].金属学报,1985,21(01):A69-A73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%