研究了0.63C-1.75Si-1.68Mn高碳硅锰TRIP钢室温低应变速率下的拉伸性能.应变速率由4.6×10-3s-1降至4.6×10-6s-1时,高碳硅锰TRIP钢伸长率由14%～15%提高到22%左右;屈服强度由1 015MPa提高到1 198MPa;抗拉强度由1 448MPa提高到1 546MPa;拉伸试样中残留奥氏体量减少,这表明在低应变速率下应变诱导相变、相变诱发塑性能充分进行.因此,该钢种特别适合于用做岩石蠕变条件下工作的煤巷超高强度锚杆材料.
参考文献
| [1] | 侯朝炯;郭励生;勾攀峰.煤巷锚杆支护[M].徐州:中国矿业大学出版社,1999 |
| [2] | David N Bigby .Developments in British rockbolting technology[J].Coal International,1997,245:111-116. |
| [3] | Hurt K .New developments in rockbolting[J].Colliery Guardian,1994,242:133-139. |
| [4] | 杨东方;曲敬信 等.奥氏体-贝氏体钢的显微组织和力学性能[J].中国矿业大学学报,1993,22(03):47-50. |
| [5] | 陈炎光;陆士良.中国煤矿巷道围岩控制[M].徐州:中国矿业大学出版社,1994:45-54. |
| [6] | Joseph Winlock .The influence of the rate of deformation on the tensile properties of some plain carbon sheet steels[J].Journal of Trauma,1953,197:797-803. |
| [7] | 李壮,李伟.应变速率对硅锰系TRIP结构钢力学性能的影响[J].热加工工艺,2001(04):8-10. |
| [8] | Sugimoto K;Misu M;Kobayashi M .Effects of second phase morphology on retained austenite morphology and tensile properties in a TRIP-aided duel-phase steel sheet[J].ISIJ International,1993,33(07):775-782. |
| [9] | 栾道成.高强韧性奥氏体-贝氏体双相钢接触疲劳特性研究[J].热加工工艺,1993(03):38. |
| [10] | 徐祖耀.马氏体相变与马氏体[M].北京:科学出版社,1999 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%