采用超音速微粒轰击方法对40Cr调质钢进行了表面纳米化处理.X射线衍射、透射电子显微镜和纳米压痕试验结果表明,表面纳米化层深达20μm,平均纳米压痕硬度比纳米化前提高2倍以上,达到8.0GPa.在表面纳米化试样表面至250μm的区域内存在残余压应力,最大残余压应力位于表面纳米化层与过渡区的分界线附近.
参考文献
[1] | Lu K;Lu J .Surface nanocrystallization of metallic materials-presentation of the concept behind a new approach[J].Journal of Materials Science and Technology,1999,15:193-197. |
[2] | Tong W P;Tao N R;Wang Z B et al.Nitriding iron at iower temperatures[J].Science,2003,299:686-688. |
[3] | Lu K;Lu J;Tao NR;Sui ML .Surface nanocrystallization of iron induced by ultrasonic shot peening[J].Nanostructured Materials,1999(4):433-440. |
[4] | N. R. Tao;Z. B. Wang;W. P. Tong;M. L. Sui;J. Lu;K. Lu .An investigation of surface nanocrystallization mechanism in Fe induced by surface mechanical attrition treatment[J].Acta materialia,2002(18):4603-4616. |
[5] | G. Liu;S.C. Wang;X.F. Lou .LOW CARBON STEEL WITH NANOSTRUCTURED SURFACE LAYER INDUCED BY HIGH-ENERGY SHOT PEENING[J].Scripta materialia,2001(8-9):1791-1795. |
[6] | G. Liu;J. Lu;K. Lu .Surface nanocrystallization of 316L stainless steel induced by ultrasonic shot peening[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1):91-95. |
[7] | 熊天英,刘志文,李智超,吴杰,金花子,李铁藩.超音速微粒轰击316L不锈钢表面纳米化的研究[C].2002年材料科学与工程新进展(2002年中国材料研讨会:论文专辑),2002:203-207. |
[8] | X.Wu;N. Tao;Y. Hong .Microstructure and evolution of mechanically-induced ultrafine grain in surface layer of AL-alloy subjected to USSP[J].Acta materialia,2002(8):2075-2084. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%