对纯镍及其表面离子注钇试样在1 000℃空气中的恒温氧化和循环氧化行为进行了研究.用扫描电镜(SEM)和透射电镜(TEM)对氧化膜的表面形貌及结构进行了观测.此外,用声发射(AE)技术研究了氧化膜/基体界面上缺陷的分布情况,并用激光拉曼(Raman)谱对注钇引起的膜内应力变化进行了测量.结果表明:离子注钇降低了NiO氧化膜的生长速率,提高了镍的抗氧化性能;离子注钇减小了表面NiO的晶粒尺寸,降低了膜内压应力水平;离子注钇还减小了氧化膜/基体界面缺陷的平均尺寸和数目,因而极大地提高了镍表面NiO氧化膜的粘附性和保护性.
参考文献
| [1] | Evans H E;Lobb R C .Condition for initiation of oxide scale cracking and spallation[J].Corrosion Science,1984,24(01):209-216. |
| [2] | Evans A G;Cannon R M .Stress and decohesion of oxide scales[J].Materials Science Forum,1989,43(03):243-249. |
| [3] | Zhang Y F;Shores D A .Spallation of oxide scales formed on Ni-30Cr alloy[J].Oxidation of Metals,1993,40(03):529-536. |
| [4] | Birnie J;Cragga C .Ex situ and in situ determination of stress distributions in chromium oxide films by Raman microscopy[J].Corrosion Science,1992,33(02):1-6. |
| [5] | Jin H M;Li T F .Influence of yttrium implantation on oxidation behavior of Co-40Cr alloy[J].Journal of Rare Earths,1999,17(01):34-38. |
| [6] | 靳惠明,张林楠,李美栓,李铁藩.Rare Earth Effects on Adhesion of Cr2O3 Oxide Scale |
| [7] | 孙晓东;王佩璇 .离子注入纯铁表面微观结构研究[J].材料科学与工程,1997,15(02):45-49. |
| [8] | 李铁藩.金属高温氧化和热腐蚀[M].北京:化学工业出版社,2003:226-260. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%