对四种高碳型Fe-Cr-C耐磨堆焊层显微组织中初生碳化物和共晶碳化物的形态进行了研究,分析了碳对显微组织的影响.结果表明:随含碳量的增加或铬碳比的降低,初生碳化物数量越来越多,且共晶碳化物体积增加,生长密度减少.柱状初生碳化物的横截面与纵截面硬度不同,横截面平均硬度为1 616.0HV,纵截面的为1 186.1HV.碳对耐磨堆焊层的组织起着重要作用.