对等离子喷涂NiCr-Cr3C2/Ni45Cr涂层的过热器管材12Cr2MoWVTiB(钢研102)在现场运行3万h后取样,与无涂层锅炉管材及未运行过的原始锅炉管材进行了高温持久强度对比试验.结果表明:涂层锅炉管持久强度性能明显优于无涂层保护炉管,据此进一步分析讨论了燃煤烟气的热腐蚀对钢研102管材持久强度的影响及涂层防护机制.
参考文献
| [1] | 冯砚厅.102钢管材持久强度的研究[J].河北电力技术,1995(01):25-28. |
| [2] | RappRobertA .Hot corrosion of materials: a fluxing mechanism[J].Corrosion Science,2002,44:209-221. |
| [3] | N. Eliaz;G. Shemesh;R.M. Latanision .Hot corrosion in gas turbine components[J].Engineering failure analysis,2002(1):31-43. |
| [4] | HigueraHV;Horlock A J;Harris S J.Microstructure and corrosion behaviour of HVOF Sprayed Nickel-based amorphous/nanocrystalline alloys[A].Nice,1998:665-670. |
| [5] | BergerLM;Yuoristo P;Mantyla T.A study of oxidation behaviour of WC-Co, Cr3C2, Ni-Cr and TiC-Ni-based materials in thermal spray processes[M].Nice,1998:75-82. |
| [6] | 石德珂;金志浩.材料力学性能[M].西安:西安交通大学出版社,1998 |
| [7] | Toloczko MB.;Hamilton ML.;Maloy SA. .High temperature tensile testing of modified 9Cr-1Mo after irradiation with high energy protons[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2003(0):200-206. |
| [8] | 张允书;李选明;史良权 等.K25O4-Na2SO4沉积引起的Fe-Cr合金的低温热腐蚀[J].中国腐蚀与防护学报,1991,11(01):18-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%