在不同温度下测试了X70管线钢动态断裂韧度K1d、J1d和止裂韧度K1a以及夏氏V型缺口冲击韧度Ak,对三者的关系进行了分析.结果表明:温度和加载速率都对断裂韧度产生影响;加载速率变化引起的韧-脆断裂转变具有热激活特征,在热激活分析基础上,在应力强度因子速率K=15 MPa·m1/2s-1条件下,得出断裂韧度、止裂韧度和冲击韧度三者的关系:Ak=4.84×106T-2.8K1d(或K1a).可以用小试样Ak数据计算得到K1d和K1a.
参考文献
| [1] | Schwartz C W;Bass B R .Rack speed relations in inferred from large sen specimen[J].Engineering Fracture Mechanics,1989,34(5-6):1209-1223. |
| [2] | Liu Y N;Zhou H J .Ductile to brittle fracture transition of a plain carbon steel and its thermal activation model[J].Engineering Fracture Mechanics,1994,48:773-782. |
| [3] | 柳永宁,冯耀荣,宋小龙,王雪元,庄传晶,马秋荣.X65管线钢的动态断裂行为研究[J].西安交通大学学报,2001(11):1171-1174. |
| [4] | Holzmann M;Dlouhy I;Brumovsky B .Measurement of fracture toughness transition behaviour of Cr-Ni-Mo-V pressure vessel steel using pre-cracked Charpy specimen[J].International Journal of Pressure Vessels and Piping,1999,76:591-598. |
| [5] | Eiber R;Carlson L;Leis B.Fracture Control Requirements for Gas Transmission pipelines[A].Calgary,Caneda:ASME,1998 |
| [6] | Liu Y N;Song X L .Dynamic fracture study of nylon-6 at different temperature[J].Journal of Materials Science Letters,1995,15:1032-1033. |
| [7] | Barsom J M .The development of AASHTO fracture toughness requirements for bridges steels[J].Engineering Fracture Mechanics,1975,7(03):605-618. |
| [8] | Barsom J M;Rolfe S T.Correlation between K1c and Charpy V-Notch Test Results on the Transition Temperature Rang[A].Philadelphia:SATM,1979:281-302. |
| [9] | Begley J A;Logsdon W A.Correlation of Fracture Toughness and Charpy Properties for Rotor Steels[A].Pittsbough:Westinghouse Research Laboratory,1971 |
| [10] | Li H L.Hot Topic in Study and Application of Steel Line Pipe for Nature Gas Transportation[A].Beijing:Beijing Petroleum Industry Press,2001:3-19. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%