采用一种自制的WC-Co基合金作轧钢导卫辊材料,在轧制2 000 t 45钢后用SEM和洛氏硬度计等对其表面形貌及硬度进行了分析和研究.结果表明:合金的主要磨损机制是体积塑性变形、犁沟效应和疲劳磨损.硬度由使用前的56 HRC下降到49 HRC,硬度下降的主要原因是合金表面部分晶粒在(受到冲击滑动摩擦作用)高速剪切变形条件下发生了动态再结晶,形成了200nm左右的细小晶粒.微细晶粒形成符合一种渐进式位相向差亚晶合并再结晶机制.
参考文献
[1] | Deshpande M V;Saxena J P;Kumar P .Development of guide roller material for steel wire-rod mill[J].International Journal of Refractory Metals and Hard Materials,1997,15(1-3):151-155. |
[2] | K. Zhang .Wear of cobalt-based alloys sliding in molten zinc[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(1/6):545-555. |
[3] | 魏世忠.复合金属材料导卫板的研制与应用[J].轧钢,1994(06):49-51. |
[4] | Stewart D.A.;McCartney D.G.;Shipway P.H. .Abrasive wear behaviour of conventional and nanocomposite HVOF-sprayed WC-Co coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(2):789-798. |
[5] | Reshetnyak H;Kubarsepp J .Structure sensitivity of wear resistance of hardmetals[J].International Journal of Refractory Metals and Hard Materials,1997,15(1-3):89-98. |
[6] | Allen C.;Williams J.;Pugsley VA.;Sheen M. .The wear of ultrafine WC-Co hard metals[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(1):604-610. |
[7] | 符寒光;刘金海.符合轧钢机导卫板的研制[J].中国铸造装备与技术,1998(05):30-32. |
[8] | Dattatraya P D;William J W .Shock response of heavy tungsten alloy[J].International Journal of Plasticity,1999,15(12):1291-1309. |
[9] | A. Parasiris;K. T. Hartwig .FORMATION/CONSOLIDATION OF WC-Co CERMETS BY SIMPLE SHEAR[J].Scripta materialia,2000(9):875-880. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%