通过分析影响单晶叶片低周疲劳寿命的主要因素,对循环塑性应变能的计算方法进行了研讨,认为构成塑性应变能的主要因素应包括循环等效应力范围、全应变范围、晶向参数和平均应力等影响参量,它们与塑性应变能之间呈幂函数关系.利用试验数据对循环塑性应变能与镍基单晶合金低周疲劳寿命之间的相关性进行定量分析,结果表明:循环塑性应变能与镍基单晶合金低周疲劳寿命之间存在着比较密切的相关关系.
参考文献
| [1] | Li S X;Smith D J .High temperature fatigue-creep behaviour of single crystal SRR99 nickel base superalloys:Part 1-Cyclic mechanical response[J].Fatigue & Fracture of Engineering Material & Structure,1995,18:617-629. |
| [2] | Li S X;Smith D J .High temperature fatigue-creep behaviour of single crystal SRR99 nickel base superalloys:Part 2-Fatigue-creep life behaviour[J].Fatigue & Fracture of Engineering Material & Structure,1995,18:631-643. |
| [3] | 童小燕,孙秦,董聪.用循环滞回能参量构造低周疲劳损伤演化规律[C].第五届全国疲劳学术会议论文集,1991:192～197页. |
| [4] | 姜风春,刘瑞堂,刘殿魁.一个用于低周疲劳寿命预测的损伤函数[J].应用数学和力学,1999(12):1275-1280. |
| [5] | Mitsuru Kanda;Masao Sakane;Masateru Ohnami;Tadashi Hasebe .High temperature multiaxial low cycle fatigue of CMSX-2 Ni-base single crystal superalloy[J].Journal of engineering materials and technology,1997(2):153-160. |
| [6] | 丁智平,刘义伦,尹泽勇,杨治国,成晓鸣.镍基单晶高温合金的屈服准则研究[J].机械强度,2004(02):175-179. |
| [7] | 丁智平,刘义伦,尹泽勇,杨治国,成晓鸣.面心立方晶体单晶材料弹塑性本构模型[J].中南大学学报(自然科学版),2004(03):423-428. |
| [8] | Nissley D M;Meyer T G .Life prediction and constitutive models for engine hot section anisotropic materials program[R].NASA-CR-189222,1992. |
| [9] | 周复恭;黄运成.应用线性回归分析[M].北京:中国人民大学出版社,1989 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%