在系列夏比冲击试验的基础上,使用OM、SEM、TEM等方法分析了国产X70管线钢断口分离现象产生的机理及其对性能的影响.研究表明:脆性带状组织及夹杂物是造成X70管线钢断口分离现象的主要原因;断口分离可使韧脆转变温度降低;X70管线钢中带状组织的氢致开裂(HIC)敏感性较高,为HIC的成核及扩展提供了便利场所.
参考文献
| [1] | F 布赖恩皮克林.材料科学与技术丛书,第七卷--钢的组织与性能[M].北京:中国科学技术出版社,1999:131. |
| [2] | Wilkowski G M;Maxey W A;Eiber R J .Use of the DWTT energy for predicting ductile frature behavior in controlledrolled steel line pipes[J].Canadian Metallurgical Quarterly,1980,19(01):59-77. |
| [3] | Feldmann U;Pellini W S.Mechanical and toughness properties of separation-free HSLA linepipe steels for arctic conditions[A].,1983:107. |
| [4] | Kazutoshi Kunishige;Fukuda M;Sugisawa S .Separations occuring in controlled rolled hot strips[J].Transactions of the Iron and Steel Institute of Japan,1979,19(01):324-331. |
| [5] | Embury J D;Petch N J;Wraith A E et al.The fracture of mild steel laminates[J].Transactions of the Metallurgical Society of AIME,1967,239:114-118. |
| [6] | 高惠临.管线钢一组织性能焊接行为[M].西安:陕西科学技术出版社,1995:36-38. |
| [7] | 乔利杰;王燕斌;褚武扬.应力腐蚀机理[M].北京:科学出版社,1993:49. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%