用钨极氩弧焊方法在A304不锈钢基体上堆焊Fe3Al合金,对其相组成进行了XRD分析,对堆焊试样在750℃和950℃温度下分别进行了Na2SO4盐和NaCl盐的热腐蚀试验.结果表明:堆焊层金属主要由Fe3Al相构成,仅含有少量的α-Fe固溶体;堆焊层金属在NaCl盐中的热腐蚀程度明显高于在Na2SO4盐中的腐蚀,且堆焊层与基体的熔合区是最薄弱的区域.
参考文献
| [1] | 朱日彰;何业东;齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995:238. |
| [2] | 范润华,孙康宁,尹衍升,包志臣.Fe3A1金属间化合物的机械合金化[J].机械工程学报,2000(08):55-58. |
| [3] | Rabin B H;Wright J K;Wright R N et al.Grain growth behavior in Fe3Al alloys fabricated by different methods[J].Journal of Materials Research,1994,9(06):1384-1391. |
| [4] | David S A;Zacharia T .Weldability of Fe3Al-type aluminide[J].Welding Journal,1993,72(05):201-207. |
| [5] | David S A;Horton J A .Weldability of iron aluminides[J].Welding Journal,1989,68(09):372-382. |
| [6] | 高德春,杨王玥,董敏,黄继华,孙祖庆.Fe-Al基金属间化合物的焊接性[J].金属学报,2000(01):87-92. |
| [7] | 曲敬信;汪泓宏.表面工程手册[M].北京:化学工业出版社,1998:694-739. |
| [8] | Mckamey C G;DeVan J H;Tortorelli P E et al.Areview of recent development in Fe3Al-based alloys[J].Journal of Materials Research,1991,6(08):1779-1805. |
| [9] | Lee WH;Lin RY .Oxidation, sulfidation and hot corrosion of intermetallic compound Fe sub 3 Al at 605 deg C and 800 deg C[J].Materials Chemistry and Physics,1999(3):231-242. |
| [10] | Das D.;Balasubramaniam R.;Mungole MN. .Hot corrosion of Fe3Al[J].Journal of Materials Science,2002(6):1135-1142. |
| [11] | 李远士,牛焱,吴维(山文).金属材料的高温氯化腐蚀[J].腐蚀科学与防护技术,2000(01):41-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%