采用弯曲疲劳和拉-压疲劳试验,比较了45钢基体上真空熔覆镍基合金/WC复合涂层试样在不同应力状态下的疲劳强度,并与45钢基体材料进行了对比.结果表明:在弯曲疲劳时,在相同寿命的条件下,正火后涂层试样比无涂层试样的承载能力提高80 MPa左右;当N＜3×104时拉-压疲劳时,涂层试样的疲劳强度小于无涂层试样,而N＞3×104时拉-压疲劳时,则相反;在相同寿命的条件下,涂层试样的弯曲疲劳强度比拉-压疲劳大75 MPa左右,而无涂层试样则大25 MPa左右.
参考文献
| [1] | 林晨,黄新波,林化春,王德俊.真空熔烧Co基合金-WC复合涂层耐磨性研究[J].机械工程材料,2003(06):40-42,45. |
| [2] | 王俊英,闫石,焦耀斌.真空熔烧镍基合金-碳化铬复合涂层抗热疲劳性能的研究[J].热加工工艺,2001(01):14-16. |
| [3] | Sobolev V V;Guilemany J M;Miguel J R et al.Investigation of the development of coating structure during high velocity oxy-fuel(HVOF) spraying of WC-Ni powder particles[J].Surface and Coatings Technology,1996,82:114-120. |
| [4] | Stewart D.A.;McCartney D.G.;Shipway P.H. .Abrasive wear behaviour of conventional and nanocomposite HVOF-sprayed WC-Co coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(2):789-798. |
| [5] | 林化春;丁润刚 .镍基合金-碳化铬复合涂层固体界面的结合问题[J].钢铁研究学报,1996,8(01):33-36. |
| [6] | 林晨,王德俊,林化春,王雷.镍基-碳化铬硬面复合涂层的疲劳强度[J].钢铁研究学报,2002(06):69-71. |
| [7] | 林晨.调质对钴基碳化钨复合涂层疲劳强度的影响[J].表面技术,2004(05):22-23,34. |
| [8] | 林晨,王德俊,林化春.调质对Ni基合金+WC复合涂层疲劳强度的影响[J].兵器材料科学与工程,2004(01):30-33. |
| [9] | 李志超;董允 .WC-Co YG13C硬质合金热处理工艺研究[J].机械工程材料,1991,25(04):43-48. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%