分别将W18Cr4V高速钢和YG8硬质合金作为衬底材料,用直流磁控溅射和射频磁控溅射法制备了CNx薄膜,用划痕法测定了薄膜和衬底材料之间的膜基结合力.结果表明:YG8硬质合金作为衬底材料时薄膜的膜基结合力较高;对YG8硬质合金衬底材料进行适当的腐蚀处理或溅射一层TiN中间层,薄膜的膜基结合力明显提高;对于两种衬底材料,射频磁控溅射法制备的薄膜膜基结合力明显高于直流磁控溅射法制备的薄膜.
参考文献
| [1] | Liu A Y;Cohen M L .Prediction of new low compressibility solids[J].Science,1989,245:841-842. |
| [2] | Liu A Y;Cohen M L .Structural properties and electronic structure of low compressibility material β-Si3N4 and β-C3N4[J].Physical Review B:Condensed Matter,1990,41(15):10727-10374. |
| [3] | Nesladek M;Vandiererdonck K;Quaeyhagens C et al.Adhesion of diamond coatings on cemented carbide[J].Thin Solid Films,1995,270:184-188. |
| [4] | 宋建华,苗晋琦,张恒大,陈利民,刘志龄,唐伟忠,吕反修,张玉英.硬质合金金刚石涂层工具基体前处理有效方法探讨[J].金刚石与磨料磨具工程,2002(05):8-11. |
| [5] | M. A. Monclus;D. C. Cameron;A. K. M. S. Chowdhurry .Electrical properties of reactively sputtered CN_x films[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1999(12):94-100. |
| [6] | 李俊杰,王欣,卞海蛟,郑伟涛,吕宪义,金曾孙,孙龙.磁控溅射CNx薄膜的附着力、粗糙度与衬底偏压的关系[J].发光学报,2003(03):305-308. |
| [7] | 吴大维,付德君,毛先唯,叶明生,彭友贵,范湘军.C3N4/TiN交替复合膜的微结构研究[J].物理学报,1999(05):904-912. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%