研究了高能球磨与热压烧结制备TiAl基合金的工艺.结果表明:在同一热压烧结工艺下,球磨时间越长,烧结试样的密度越大.以球磨40 h的粉末为原料,经1 300 ℃热压烧结可获得密度高达3.971 g/cm3的近全致密的TiAl基合金,且得到的TiAl基合金晶粒较小,组织均匀.
参考文献
| [1] | Kim Y W.Ordered intermetallic alloys,part Ⅲ:gamma titanium aluminides[J].Jom,1994(07):30-39. |
| [2] | Lee T K;Mosunov E I;Hwang S K.Consolidation of a gamma TiA1-Mn-Mo alloy by elemental powder metallurgy[J].Material Science and Engineering,1997(04):128-131. |
| [3] | L.M. Hsiung;T.G. Nieh .Microstructures and properties of powder metallurgy TiAl alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):1-10. |
| [4] | N. Hoo;P.S. Goodwin;R.M. Brydson .Microstructural Control in a Gamma-TiAl Alloy by MA and HIPing[J].JOM,1996(7):40-41. |
| [5] | 王尔德,胡连喜,李小强.高能球磨Ti/Al复合粉体的反应烧结致密行为[J].粉末冶金技术,2003(05):259-263. |
| [6] | Dutkiewicz J.;Maziarz W.;Heinrich H.;Kostorz G. .Structure of Ti-Al-Nb intermetallics produced by mechanical alloying and hot-pressing techniques[J].Materials Chemistry and Physics,2003(2/3):414-416. |
| [7] | Kim Y W .Wrought TiAl Alloy Design[J].Transactions of Nonferrous Metals Society of China,1999,9(z1):298-308. |
| [8] | Prajina B;Pascal B .Nanocrystalline TiAl powders synthesized by high-energy ball milling:effect of milling parameters on yield and contamination[J].Alloys and Compounds,2004,368:187-196. |
| [9] | Bohm A;Kidback B .Investigation of swelling behaviour of Ti-Al elemental powder mixtures during reaction sintering[J].Zeitschrift fur Metallkunde,1998,89(02):90-94. |
| [10] | Y. WU;S. K. HWANG;J. W. MORRIS JR. .Development and Elemental Powder Metallurgy of a Y-Containing Two-Phase TiAl Alloy[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2003(10):2077-2087. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%