喷射沉积多孔铝合金板坯由于有孔洞且缺乏良好的冶金结合,直接轧制时易出现板坯表面裂纹及边裂.为此研究了外框限制轧制工艺对喷射沉积多孔材料5A06和8009铝合金板坯轧制组织和力学性能的影响.结果表明:外框限制轧制工艺提高了喷射沉积多孔材料的致密度,避免了轧制过程中裂纹的形成,有效地改善了喷射沉积板坯的轧制性能及材料的力学性能.
参考文献
| [1] | Skinner D J;Bye R L;Raybould D et al.Dispersion strengthened Al-Fe-V-Si alloy[J].Scripta Metllurgica,1986,20(06):867-872. |
| [2] | Gilman P S;Zedails M S;Pehier J M.Rapidly solidified aluminum-transition metal alloys for aerospace application[A].Atlanta,1988 |
| [3] | YUAN Wu-hua;CHEN Zhen-hua;HUANG Pei-yun .Preparation of heat-resistant aluminum alloy pipe blanks by multi-layer spray deposition[J].Transactions of Nonferrous Metals Society of China,2000(4):460-464. |
| [4] | Hariprasad S;Saotry S M L;Jerina K L et al.Microstructures and properties of dispersion-strengthed high-temperature Al-8.5Fe-1.2V-1.7Si alloys produced by atomized melt deposition process[J].MetallTrans A,1993,24A(04):865-875. |
| [5] | 詹美燕 .喷射沉积材料压缩和轧制变形规律研究[D].湖南大学,2005. |
| [6] | 陈振华,詹美燕,夏伟军.改善喷射沉积耐热铝合金板坯轧制成形性能的研究[J].湖南大学学报(自然科学版),2003(05):10-14. |
| [7] | 詹美燕,夏伟军,袁武华,傅定发,陈振华.喷射沉积耐热铝合金8009板坯轧制工艺及其对板材组织性能的影响[J].热加工工艺,2004(02):38-40. |
| [8] | 陈振华,严红革,陈刚,张福全,胡仲勋,傅杰新.多层喷射沉积的装置和原理[J].湖南大学学报(自然科学版),2001(05):20-28. |
| [9] | 田荣璋.铝合金及其加工手册[M].长沙:中南大学出版社,2000 |
| [10] | 詹美燕,匡勇,周明,夏伟军.多孔金属及合金成形过程中的致密化与变形理论研究[J].稀有金属与硬质合金,2002(04):42-47. |
| [11] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1981 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%