利用袋压工艺、采用单向碳纤维/环氧复合材料补片对含中心裂纹的铝合金板进行了修补,测试了胶接修补前后板的静态力学性能和疲劳性能.结果表明:经过修补后,铝合金板抵抗静态拉伸破坏和疲劳破坏的能力均有显著的提高,其静态抗拉强度从258.35 MPa增加到349.69MPa,提高了35.35%;其疲劳寿命从25 446周次增加到63 868周次,提高了1.51倍,裂纹起始扩展速率从0.34μm/周次降低到0.16μm/周次,临界裂纹长度从20.20 mm增加到28.05 mm.
参考文献
| [1] | 陈绍杰.复合材料结构修理指南[M].北京:航空工业出版社,2001 |
| [2] | Baker A A.Bonded repair of aircraft structure[M].Netherlands Dordrecht:Martinus Nijhoff Publisher,1988 |
| [3] | 薛克兴.复合材料结构的损伤与修补[M].北京:航空工业出版社,1992 |
| [4] | Baker A A.Fiber composite repair of cracked metallic aircraft components:Practical and basic sspects[J].Composite,1987(04):293-307. |
| [5] | Baker A.Bonded composite repair of fatigue-cracked primary aircraft structure[J].COMPUTERS & STRUCTURES,1994(47):431-443. |
| [6] | Michael L O.Carbon composite repairs of helicopter metallic primary structure[J].COMPUTERS & STRUCTURES,1993(25):557-565. |
| [7] | 陈绍杰.用复合材料技术修理金属飞机结构[J].航空制造工程,1996(09):33-34. |
| [8] | 邢素丽,曾竟成,杨孚标,肖加余,江大志,彭超义.复合材料修复铝合金构件的刚度分析和试验验证[J].机械工程材料,2005(01):13-15. |
| [9] | 徐建新,刘艳红,周煊,孙智强.损伤金属结构的复合材料胶接修补实验研究[J].南京航空航天大学学报,2001(01):96-99. |
| [10] | 复合材料补片胶接修理技术的研究进展[J].航空学报,1999(04):381. |
| [11] | 航空航天工业部科学技术研究院.复合材料设计手册[M].北京:航空工业出版社,1990 |
| [12] | Wang Q Y;Pidaparti R M.Static characteristics and fatigue behavior of composite repaired aluminum plates[J].COMPUTERS & STRUCTURES,2002(56):151-155. |
| [13] | Lee J J;Seo D C.Fatigue crack growth behavior of cracked aluminum plate repaired with composite patch[J].COMPUTERS & STRUCTURES,2002(57):323-330. |
| [14] | J. J. Schubbe;S. Mall .Investigation of a cracked thick aluminum panel repaired with a bonded composite patch[J].Engineering Fracture Mechanics,1999(3):305-323. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%