将不同数量的锰添加到Al-2%Fe合金中,进行电磁过滤并浇注试样,研究了合金中富铁相的形貌和力学性能.结果表明:初生Al3Fe相的形貌发生了明显的变化,当锰、铁的摩尔比为1.3～1.5时,针状的富铁相基本消失,取而代之的是块状.锰变质后,抗拉强度比变质前的126 MPa提高了20～30 MPa,伸长率达到22.9%.变质的熔体通过电磁过滤后,由于铁相基本上被去除,合金的伸长率可以达到29.2%,而抗拉强度降低为131 MPa.
参考文献
| [1] | 印飞,杨江波,孙宝德.铝硅合金中的六角形铁相[J].上海交通大学学报,2001(03):477-480. |
| [2] | Narayanan L A;Samuel F H;Gruzleski J E .Crystal2lization behavior of iron-containing inter-metallic compound in 319 aluminum alloy[J].Metallurgy and Materials Transactions A,1992,25A:1761-1766. |
| [3] | Sigworth G K;Shivkuman S;Apelian D .The influence of molten metal processing on mechanical properties of cast Al-SiMg alloy[J].AFS Transactions,1989,139:811-824. |
| [4] | Awano Y;Shimizu Y .Non-equilibrium crystallization of Al-SiFe compound in melt-superheated Al-Si alloy casting[J].AFS Transactions,1990,176:889-896. |
| [5] | Couture A .Iron in aluminum casting alloys--A literature survey[J].AFS Transactions,1981,11:9-17. |
| [6] | Muali S;Raman K S;Murthy K S S .Morphological studies on β-FeSiAl5 phase in Al-7Si-0.3Mg alloy with trace addition of Be,Mn,Cr and Co[J].Materials Characterization,1994,33:99-112. |
| [7] | 疏达,孙宝德,李天晓,张雪萍,周尧和.铝熔体中夹杂物形状与取向对其电磁分离的影响[J].金属学报,2000(09):956-960. |
| [8] | 李克,孙宝德,李天晓,疏达,丁文江,周尧和.利用高频磁场分离Al熔体中的非金属夹杂[J].金属学报,2001(04):405-410. |
| [9] | 钟云波;任忠鸣;邓康 等.行波磁场净化液态金属时矩形管及三角管内夹杂除去效率的理论分析[J].金属学报,1999,5(05):503-508. |
| [10] | 朴杓;森平淳志;佐々健介 等.电磁力を利用した溶融金属中介在物の除去[J].铁と钢(日本),1994,80(05):31-36. |
| [11] | 李克,孙宝德,李天晓,疏达,丁文江,周尧和.利用高频磁场分离Al熔体中的非金属夹杂[J].金属学报,2001(04):405-410. |
| [12] | Mondolfo L F;Wang Z T;Zhang Z L.Structures and properties of aluminum alloys[M].北京:冶金工业出版社,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%