采用热模拟试验机对一种自行研制的高强度易切削锌基合金进行了等温热压缩试验.结果表明:该锌合金热压缩变形流变应力随变形温度升高而减小,随应变速率增大而增大,变形材料内部的温升随应变速率的增大而加剧;可用包含变形温度、应变速率和变形程度的Zener-hollomon模型来真实描述该锌合金高温变形的流变行为.
参考文献
| [1] | 孙连超;田荣璋.锌及锌合金物理冶金学[M].长沙:中南工业大学出版社,1994 |
| [2] | 蔡强.锌合金[M].长沙:中南工业大学出版社,1987 |
| [3] | 龚冰;王涛;张红梅.新型锌基合金在汽车上的应用[J].重型汽车,1997(04):25-26. |
| [4] | 刘政,朱应禄,陈慈诰.稀土锌合金凝固组织与力学性能的研究[J].南方冶金学院学报,2002(01):23-27. |
| [5] | 林高用,肖弦,郑小燕.锌合金切削性能的研究[J].矿冶工程,2006(05):96-98. |
| [6] | 牛济泰.材料和热加工领域的物理模拟技术[M].北京:国防工业出版社,1998 |
| [7] | Mcqueen H J;Jonas J J.Recovery and recrystallization in the hot-working of aluminum alloys[M].New York:Academic Press,Inc,1975:393-493. |
| [8] | Wang W A;Jonas J J .Flow of plastic and visco-plastic solids in hot forming process[J].Transactions of the Metallurgical Society of AIME,1968,242:2271-2279. |
| [9] | Sah J P;Richardson G J;Sellar C M .Plane strain compression testing at elevated temperature[J].Journal of the Australian Institute of Metals,1969,14:292-301. |
| [10] | Castro-Fernandez F R;Sellars C M;Whiteman J A.Changes of flow stress and micro-structure during hot deformation of Al-1Mg-1Mn[J].Materials Science and Technology,1990(06):453-468. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%