将粒径为1~5μm的原料铜粉置入辊压振动磨中,经振动研磨后得到纳米铜粉,通过X射线多晶衍射仪和扫描电子显微镜对其进行了分析.结果表明:得到的纳米铜粉晶格类型仍为面心立方晶格,结构参数和化学成分没有发生变化;随着研磨时间的增加,粉末的平均粒径越来越小,粒度分布趋于均匀,研磨6 h以后,平均粒径在100 nm左右.
参考文献
[1] | Chosh J .Preparation of Cu,Ag,Fe and Al nanopartides by the exploding wire technique[J].Proceedings of the Indiana Academy of Science,2003,115:499-508. |
[2] | Tomita Y;Hasegawa Y;Kobayashi K .Nano-scale Cu metal patterning by using an atomic force microscope[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(1/4):107-110. |
[3] | HanWK;ChoiJW;HwangGH et al.Fabrication of Cu neno panicles by direct electrochemical reduction from CuP neno particles[J].Applied Surface Science,2006,252:2832-2838. |
[4] | Dragomir IC;Gheorghe M;Thadhani N;Snyder RL .X-ray peak profile analysis of crystallite size distribution and dislocation type and density evolution in nano-structured Cu obtained by deformation at liquid nitrogen temperature[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):158-162. |
[5] | Wang Shulin.Impact chaos control and stress release -A key for development of ultra fine vibration milling[J].自然科学进展(英文版),2002(05):336-341. |
[6] | WANG Shulin,LI Shengjuan,DU Yanchen,XU Bo,LI Laiqiang,ZHU Yan.Nanostructural evolution of Zn by dry roller vibration milling at room temperature[J].自然科学进展(英文版),2006(04):441-444. |
[7] | 王树林 .滚压振动磨[P].CN 99112092.2 |
[8] | 郑水林.超微粉体加工技术与应用[M].北京:化学工业出版社,2004 |
[9] | 王树林.一种制备纳米片状锌粉的新方法[J].矿山机械,2003(10):42-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%