采用累积叠轧焊方法在室温下加工1060工业纯铝,分析了叠轧变形前后其力学性能的变化.结果表明:随着累积叠轧道次的增加,材料的抗拉强度和显微硬度都得到提高;拉伸断口处的韧窝逐渐变小变浅,但仍为韧性断裂;轧制1道次后试样的伸长率较母材的伸长率急剧降低,随着轧制的进行伸长率变化平稳;累积叠轧5道次材料的综合力学性能较好,抗拉强度提高到210 MPa,是母材的2.41倍,显微硬度78.5 HV,是母材的2.2倍,伸长率9.3%,仅是母材的0.21倍.
参考文献
| [1] | N. Tsuji;S. Okuno;T. Matsuura .Mechanical Properties as a Function of Grain Size in Ultrafine Grained Aluminum and Iron Fabricated by ARB and Annealing Process[J].Materials Science Forum,2003(Pt.3):2667-2672. |
| [2] | Reis Ana;Carmen C;Kestens Leo .Cross-sectional texture gradients in interstitial free steels processed by accumulated roll bonding[J].Solid State Phenomena,2005,105:233-238. |
| [3] | Seong-Hee Lee;Hiroshi Utsunomiya;Tetsuo Sakai .Microstructures and Mechanical Properties of Ultra Low Carbon Interstitial Free Steel Severely Deformed by a Multi-Stack Accumulative Roll Bonding Process[J].Materials transactions,2004(7):2177-2181. |
| [4] | Kaneko S;Fukuda K;Utsunomiya H et al.Ultra grain refinement of aluminium 1100 by ARB with cross rolling[J].Materials Science Forum,2003,432(03):2649-2654. |
| [5] | Heinz Werner Hoppel;Johannes May;Mathias Goken .Enhanced Strength and Ductility in Ultrafine-Grained Aluminium Produced by Accumulative Roll Bonding[J].Advanced Engineering Materials,2004(4):219-222. |
| [6] | 王军丽,史庆南,吴承玲,张坤华.大变形异步叠轧制备超细晶铜材叠轧过程组织演变研究[J].新技术新工艺,2006(04):96-99. |
| [7] | 王耀奇,侯红亮,许荣昌,任学平.累积叠轧焊对L2纯铝力学性能影响的研究[J].锻压技术,2006(01):86-89. |
| [8] | 方建敏,张杏耀,单爱党,吴建生.累积叠轧焊不锈钢的组织和性能[J].机械工程材料,2006(08):16-18. |
| [9] | Saito Y.;Tsuji N.;Sakai T.;Utsunomiya H. .Novel ultra-high straining process for bulk materials - Development of the accumulative roll-bonding (ARB) process[J].Acta materialia,1999(2):579-583. |
| [10] | 余永宁.金属学原理[M].北京:冶金工业出版社,2000:464-469. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%