在氩气保护下,采用搅拌铸造法制备了碳纳米管(CNTs)/ZM5镁合金复合材料;测试了铸态下其高温拉伸性能,并对其显微组织和断口形貌进行了分析.结果表明:该复合材料具有良好的高温拉伸性能,在拉伸速率为1mm·min-1以及温度为473K时其抗拉强度可达117.65MPa,比基体提高了20%;当CNTs加入量为0.5%时,其最大伸长率达到8.32%,比基体提高了21.62%;在高温下该复合材料的断裂形貌主要由韧窝和撕裂棱所组成.
参考文献
| [1] | Michael M.Magnesium and Magnesium Alloys[M].Ohio:Materials Park,2000 |
| [2] | Dargusch M;Hish M;Caceres C H.Elevated temperature deformation of die cast Mg alloy AZ91[A].Mancherster;[s n],1996 |
| [3] | Iijima S .Helical microtubules of graphitic carbon[J].Nature,1991,354:56-58. |
| [4] | Baughman R H;Zakhidov A A;Heer W A .Carbon nanotubes-the route toward applications[J].Science,2002,297:787-792. |
| [5] | 李四年,宋守志,余天庆,陈慧敏,张友寿,黄晋.铸造法制备纳米碳管增强镁基复合材料的力学性能研究[J].铸造,2004(03):190-193. |
| [6] | C S Goh;J Wei;L C Lee .Development of novel carbon nanotube reinforced magnesium nanocomposites using the powder metallurgy technique[J].Nanotechnology,2006(1):7-12. |
| [7] | Goh CS;Wei J;Lee LC;Gupta A .Simultaneous enhancement in strength and ductility by reinforcing magnesium with carbon nanotubes[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1-2):153-156. |
| [8] | 赵云虎,王渠东,丁文江,曾小勤,吕宜振,朱燕萍.Be对铸造Mg合金组织和力学性能的影响[J].特种铸造及有色合金,2000(03):10-12. |
| [9] | 闵学刚,朱旻,孙扬善,薛烽.Ca对AZ91显微组织及力学性能的影响[J].材料科学与工艺,2002(01):93-96. |
| [10] | Polmear I J .Magnesium alloys and applications[J].Materials Science and Technology,1994,10:1-16. |
| [11] | Zhou S M;Zhang X B;Ding Z P et al.Fabrication and tribological properties of carbon nanotubes reinforced Al composites prepared by pressureless infiltration techniqu e[J].Composites,2006,10:1-6. |
| [12] | Kuzumaki T.;Ichinose H.;Ito K.;Miyazawa K. .Processing of carbon nanotube reinforced aluminum composite[J].Journal of Materials Research,1998(9):2445-2449. |
| [13] | 吴安如,董丽君,夏长清,武文花.稀土元素对镁合金高温力学性能的影响[J].热加工工艺,2006(04):26-30. |
| [14] | 陈礼清,郭金花,王继杰,徐永波,毕敬.原位反应自发渗透法TiC/AZ91D镁基复合材料及AZ91D镁合金的拉伸变形与断裂行为[J].稀有金属材料与工程,2006(01):29-33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%