分析了氧化膜生长机制、分布形态及变化规律,探讨氧化膜失效对辊面粗糙度和磨损状态的影响,结合济钢的生产实践提出了控制轧辊温度、降低剪切应力的改进措施,为有效控制工作辊氧化膜状态和带钢表面质量奠定了基础.
参考文献
| [1] | Lanterri V;Thomas C;Bocqet J.Black Oxide Film Generation on Work Roll s and It s Effect s on Hot2Rolling Tribological Characteristics[A].Chiba,Japan:The Iron and Steel Institute of Japan,1998 |
| [2] | Molinari A;St raffelini G;Tomasi A.Oxidation Behavior of Ledeburitic Steels for Hot Rolls[J].Materials Science and Engineering,2000 |
| [3] | Colas R;Ram?rez J;Sandoval I.Damage in Hot Roiling Work Rolls[J].Wear,1999 |
| [4] | Tsujimoto Y.High Performance High Speed Steel Roll withFine Microstructure for Resistance to Surface Deterioration[J].Current Advances in Materials and Processes,2002 |
| [5] | Li C S.Black Oxide Layer Formation and Banding in HighChromium Rolls[J].Journal of Materials Science and Technology,2000 |
| [6] | Gonzalaz V.Modeling Oxidation of Hot Rolling Work Rolls[J].Ironmaking and Steelmaking,2001 |
| [7] | Molinari A.Oxidation Behaviour of Ledeburitic Steels for Hot Rolls[J].Materials Science and Engineering,2000 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%