以待分析的铁素体不锈钢和碳棒分别作为阳极和阴极，用由阴离子交换膜隔开的三室电解池作为采样器，对该钢样进行逐层溶解，并用氧化还原滴定法测定每一层中铬的含量。经测定，厚度约为0.03mm的表层中铬的平均含量为7.82％，基体中铬的含量为17.20％，另该表层中硅的含量为1.69％，基体中硅的含量为0.0774％，即该不锈钢表层为贫铬富硅层。
The ferritic stainless steel to be analyzed and carbon rods were used as anode and cathode, respectively. The dissolver was a triple-chamber electrolyser with the membrane placed between the chambers. The stainless steel sample was dissolved by layers, and chromium content of each layer was determined by the redox titration. The average chromium content of the surface layer about 0.03 mm thick is 7.82%, and that of the matrix of the steel is 17.20%. Silicon contents of the surface layer and the matrix are 1.69% and 0.0774%, respectively. That is to say, the surface of the ferritic stainless steel is a lager of poor chromium and rich silicon.
参考文献
| [1] | 藤田辉夫;丁文华;张绪江;陈玉璋.不锈钢的热处理[M].北京:机械工业出版社,1983 |
| [2] | J N Yang;K Ou et al.[J].Anal Proc,1995,32(04):155. |
| [3] | J.Zhang,J.N.YANG.Electrolytic sampling from pure copper and common brasses Ⅰ: calculation of the mass dis-solved from the samples according to Faradat's law[J].Chinese Chemical Letters,1997(02):167. |
| [4] | 徐盘明;赵祥大.实用金属材料分析方法[M].合肥:中国科学技术大学出版社,1990:320. |
| [5] | HФ拉施柯;金钦乾;徐澄宇;马翔.钢和合金的物理-化学相分析[M].北京:国防工业出版社,1982 |
| [6] | 冶金工业部钢铁研究总院.钢和铁、镍基合金的物理化学相分析[M].上海:上海科学技术出版社,1981 |
| [7] | 王正樵;吴幼林.不锈钢[M].北京:化学工业出版社,1991 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%