LB膜作为模板可诱导晶体取向成核和外延生长,生成的晶体材料具有独特的微观结构和优异的物理化学性能.这种方法对于生物矿化现象的研究以及新颖材料合成策略的设计等方面具有重要的启示意义.本文从LB膜诱导晶体取向生长的机理及利用等方面综述了该领域研究的最新进展.
参考文献
[1] | Heywood B R;Rajam S;Mann S .[J].Journal of the Chemical Society,Faraday Transactions,1991,87(05):735. |
[2] | Heywood B R;Mann S .[J].Advanced Materials,1992,4:278. |
[3] | Mann S .[J].Nature,1988,332:119. |
[4] | Aksay I A;Tran M et al.[J].Science,1996,273:892. |
[5] | Bunker B C;Rieke P C;Tarasevich B J .[J].Science,1994,264:48. |
[6] | Mohanty R;Bhandarkar S;Estin J .[J].AICHE Journal,1990,36:1536. |
[7] | Yang J K;Fendler J H .[J].Journal of Physical Chemistry,1995,99:5505. |
[8] | Cooper SJ.;Lubetkin SD.;Sessions RB. .A new mechanism for nucleation beneath monolayer films?[J].Journal of the American Chemical Society,1998(9):2090-2098. |
[9] | Tang R K;Jing C Y;Tai Z H.[J].Journal of the Chemical Society Dalton Transactions,1997:4037. |
[10] | Landau E M;Levanon M;Sagiv J et al.[J].Nature,1985,318:353. |
[11] | Berman A;Ahn DJ;Lio A;Salmeron M;Reichert A;Charych D .TOTAL ALIGNMENT OF CALCITE AT ACIDIC POLYDIACETYLENE FILMS - COOPERATIVITY AT THE ORGANIC-INORGANIC INTERFACE[J].Science,1995(5223):515-518. |
[12] | Tissue BM. .Synthesis and luminescence of lanthanide ions in nanoscale insulating hosts [Review][J].Chemistry of Materials,1998(10):2837-2845. |
[13] | Zhao X K;Yang J;Fendler J H .[J].Journal of Physical Chemistry,1992,96:9933. |
[14] | Yang J P;Meldrum F C;Fendler J H .[J].Journal of Physical Chemistry,1995,99:5500. |
[15] | Werkman P J;Schouten A J .[J].Thin Solid Films,1998,323:251. |
[16] | Moriguchi I;Matsuo K;Kagawa S et al.[J].Journal of the Chemical Society,Faraday Transactions,1998,94(15):2199. |
[17] | Xu X.;Burch E.;Lopez GP.;Cesarano J. .TEMPLATE-ASSISTED ELECTROCHEMICAL DEPOSITION OF ULTRATHIN FILMS OF CADMIUM SULFIDE[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1997(1/2):95-102. |
[18] | Mayya K S;Patil V;Sastry M et al.[J].Thin Solid Films,1998,312:300. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%