在SrO-La2O3-B2O3体系中合成出一种新的硼酸盐化合物La2SrB10O19.La2SrB10O19的晶体结构与La2CaB10O19相同.La2SrB10O19的粉末倍频效应(SHG)大约是KH2PO4(KDP)的2倍.差热分析结果表明该化合物为非同成分熔融化合物,转熔温度约为983℃,可以用助熔剂法进行晶体生长.反射光谱研究表明La2SrB10O19的紫外吸收边在300nm左右.
参考文献
[1] | Chen C;Wu B;Jiang A;You G .A New Ultraviolet SHG Crystal β-BaB2O4[J].Science Sinica,1985,B28:235. |
[2] | Chen C;Wu Y;Jiang A et al.New Nonlinear Optical Crystal: LiB3O5[J].Journal of the Optical Society of America,1989,B6:616. |
[3] | Wu Y;Sasaki T;Nakai S et al.CsB3O5:A New Nonlinear Optical Crystal[J].Applied Physics Letters,1993,66:2614. |
[4] | Mori Y;Kuroda I;Nakajima S et al.Nonlinear Optical Properties of Cesium Lithium Borate.Jpn[J].Journal of Applied Physics,1995,34:296. |
[5] | Chen C;Wang Y;Xia Y et al.New Development of Nonlinear Optical Crystals for the Ultraviolet Region with Molecular Engineering Approach[J].Journal of Applied Physics,1995,77:2268. |
[6] | Chen C;Wang Y;Wu B;Wu K, et al.Design and Synthesis of an Ultraviolet-Transparent Nonlinear Optical Crystal Sr2Be2B2O7[J].NATURE,1995,373:322. |
[7] | Tu J;Keszler D .CsLiB6O10:A Noncentrosymmetric Polyborate[J].Materials Research Bulletin,1995,30:209. |
[8] | Wu Y;Liu J;Fu P.A New Class of Nonlinear Optical Crystals R2CaB10O19(RCB)[A].,1998:8. |
[9] | Chen C;Wu Y;Li R .The Anionic Group Theory and its Applications in Borates[J].International Reviews in Physical Chemistry,1989,8:865. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%