利用助溶剂法,已经生长出15mm×25mm×60mm的大尺寸NdP5O14(NPP)晶体.用高分辨X射线衍射术对自发应变及铁弹畴结构进行了研究.对几个不同的反射,可在其摇摆曲线上观测到由基体畴和铁弹畴之间的取向差导致的反射峰的分离.通过反射峰分离的特点,可以确定铁弹畴结构.NPP晶体中大多数铁弹畴为a型畴,b型畴只出现在严重形变的区域. 基于NdP5O14晶体畴结构,我们分别计算了802,402和204反射的峰分离量.实验测量结果符合计算结果.另外,通过测量基体畴和铁弹畴的800反射的峰分离量我们确定了NdP5O14的自发应变是0.0082.通过结构和对称性分析,我们对这种晶体的畴结构进行了详细讨论.
参考文献
| [1] | Weber H P;Damen T C;Danielmeyer H G .Nd-Ultraphosphate Laser[J].Applied Physics Letters,1973,22:534. |
| [2] | Hu Z W;Jiang S S;Huang P Q;Wang J Y,Li L X .Direct Observation of Ferroelastic Phase Transition in Er-doped Lanthanum Pentaphosphate with Synchrotron Topography[J].Applied Physics Letters,1994,66:55. |
| [3] | Hu Z W;Huang P Q;Jiang S S .Synchrotron X-ray Topography Study of Er-doped LaP5O14 Crystal[J].Journal of Applied Physics,1993,74:7124. |
| [4] | Huang X R;Hu Z W;Jiang S S .Synchrotron Radiation Topography Studies of Twinning NdP5O14Crystal[J].Journal of Applied Physics,1994,75:7756. |
| [5] | Huang X R;Jiang S S;Hu Z W;Xu X Y,Feng D .Influence of Ion-electron Interaction on the Formation Mechaniam of Depleted Zones in Displacement Cascades in Metals[J].Physical Review B,1994,50:13194. |
| [6] | 王继扬;刘耀岗;陆宝生 .Nd1-xRexP5O14(Re＝La,Y)系列晶体生长特性研究[J].山东大学学报(理学版),1998,2(02):80. |
| [7] | Budin J P;Milatos-roufos A;Chinh N D;Leroux G .Ferroelastic Behavior of NdxLa1-xP5O14Crystals[J].Journal of Applied Physics,1975,46:2867. |
| [8] | Sapriel J .Domain-wall Orientations in Ferroelastics[J].Physical Review B,1975,12:5128. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%