用提拉法生长了高质量、大尺寸、具有混合钙钛矿结构的(La,Sr)(Al,Ta)O3晶体(LSAT),晶体尺寸达55mm×50mm.讨论了晶体生长有关工艺,并对晶体的完整性进行了初步研究.
参考文献
[1] | Tidrow S.C.;Tauber A.;Wilber W.D.;Lareau R.T.;Brandle C.D.;Berkstresser G.W.;Ven Graitis A.J.;Potrepka D.M.;Budnick J.I.;Wu J.Z. .New substrates for HTSC microwave devices[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,1997(2):1766-1768. |
[2] | Chakoumakos BC.;Urbanik M.;Luine J.;Schlom DG. .Thermal expansion of LaAlO3 and (La,Sr)(Al,Ta)O-3, substrate materials for superconducting thin-film device applications[J].Journal of Applied Physics,1998(4):1979-1982. |
[3] | Shimamura K.;Takeda H.;Kochurikhin VV.;Fukuda T.;Tabata H. .Growth and characterization of (La,Sr)(Al,Ta)O-3 single crystals as substrates for GaN epitaxial growth[J].Journal of Crystal Growth,1998(2):209-213. |
[4] | Ohta J;Fujioka H;Sumiya M et al.Epitaxial Growth of AlN on(La,Sr)(Al,Ta)O3 Substrate by Laser MBE[J].Journal of Crystal Growth,2001,225:73-78. |
[5] | Materika D;Kohler H;Laudan H et al.Mixed-perovskite Substrates for High-Tc Superconductors[J].Journal of Crystal Growth,1991,109:447-456. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%