在Ce∶Cu∶LiNbO3晶体中掺进In2O3,用CZ法首次生长In∶Ce∶Cu∶LiNbO3晶体.对晶体的抗光折变能力、红外光谱、指数增益系数、衍射效率和响应时间进行了测试,结果表明:In(3mol%)∶Ce∶Cu∶LiNbO3晶体的抗光折变能力比Ce∶Cu∶LiNbO3提高两个数量级,其OH-吸收峰由LiNbO3的3484 cm-1移到3508 cm-1,响应速度比Ce∶Cu∶LiNbO3晶体快三倍.对In∶Ce∶Cu∶LiNbO3晶体抗光折变能力提高的机理、红外光谱OH-吸收峰紫移的机理进行了研究.
参考文献
| [1] | Youwen Liu;Liren Liu;De'an Liu;Liangying Xu;Changhe Zhou .Intensity dependence of two-center nonvolatile holographic recording in LiNbO_(3):Cu:Ce crystals[J].Optics Communications: A Journal Devoted to the Rapid Publication of Short Contributions in the Field of Optics and Interaction of Light with Matter,2001(1/6):339-343. |
| [2] | Yequan Zhao;Jun Wang;Yuheng Xu .Investigation of the Holographic Storage Property and Application of Zn∶Fe∶LiNbO3[J].Ferroelectrics,253:177-183. |
| [3] | 李铭华,赵业权,许克彬,徐玉恒,韩爱珍.氧化和还原处理对Fe：LiNbO3晶体光折变效应的影响[J].科学通报,1995(21):1955-1957. |
| [4] | Kovacs L;Wohlecke M;Jovanovic A;Polgar K .Infrared Absorption Study of the OH Vibrational Band in LiNbO3 Crystals[J].Physical and Chemistry of Solids,1991,52(06):797. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%